Epitaxial aluminum nitride films on 6H-SiC (0001) were fabricated using reactive RF magnetron sputtering and post-deposition rapid thermal annealing. The electrical properties of AIN films depending on film thickness and measurement temperature have been observed. Full width at half maximum of AIN (0002) was $0.1204^{\circ}$ (about 430 arcsec) X-ray rocking curve results. The equivalent oxide thickness (EOT) of AIN film was estimated as about 10 nm and the leakage current density was within the order of $10^{-8} 4/cm^2$. The dielectric constant of AIN film estimated from the accumulation region of C-V curve measured at $300^{\circ}C$ was 8.3. The dynamic dielectric constant was obtained as 5.1 from J vs. 1/T plots at the temperature ranging from R.T. to $300^{\circ}C$ From above, estimation temperature dependance of the electrical properties of Al/AIN/SiC MIS devices was affirmed and useful data compilation for the reliabilities of SiC MIS is expected.