Electro-Optical Characterization of Hg-Free Fluorescent Lamps for LCD Backlight

LCD 배면광원용 무수은 형광램프의 전기.광학적 특성

Hg-free fluorescent lamps were fabricated and electro-optical characterization were measured for using LCD backlight. PDP phosphors, nitro-cellulose and n-butyl acetate were mixed and coated uniformly in glass tube without stain. The glass tubes were sintered at $550^{\circ}C$ for 20 minutes, vacuumed to $10^{-6}$ torr and supplied discharge gas by using a gas mixture. After various experiment about phosphors thickness and inner diameter of glass tube, the appropriate phosphors thickness and inner diameter of glass tube were obtained. The luminance and luminous efficiency of manufactured fluorescent lamps with Ne+Xe discharge gas were $6,270cd/m^2$, 13 lm/W under 75 kHz sinusoidal wave voltage, respectively.

LCD의 배면광원으로 활용될 무수은 형광램프를 제작한 다음, 전기 광학적 특성을 평가하였다. PDP 형광체, nitro-cellulose 및 n-butyl acetate를 혼합하여 유리관 내부에 얼룩 없이 균일하게 코팅하였다. 또 $550^{\circ}C$에서 20 분 동안 소성하였고, 가스혼합장치를 이용하여 $10^{-6}$ torr까지 배기시킨 다음 방전가스를 주입하여 형광램프를 완성시켰다. 형광체 두께 및 유리관 직경 등을 변화시켜 제작, 평가한 결과 이들 변수들에 대하여 최적의 값을 찾아 낼 수 있었다. 또한 Ne+Xe 방전가스를 주입하여 제작된 형광램프에 75 kHz의 정현파 전압을 공급시킨 결과 휘도 $6,270cd/m^2$, 발광효율 13 lm/W를 얻었다.