Contraction of Alpha-nickel Hydroxide Layers by Excess Coulombic Attraction of Anions

전기화학적으로 형성된 알파 상 니켈 수산화물의 층간 거리에 미치는 음이온의 영향 연구

  • Published : 2006.04.20

Abstract

In this study computer assisted instruction materials for the ‘Solution' chapter in high school chemistry II textbook were developed based on a view of particle and analyze the effect of the materials on 10th and 11th high school students. The contents of developed materials are dissolution, vapor pressure, the change of boiling point and freezing point, osmosis, and so on which are the major contents of Solution chapter in high school chemistry II textbook. Materials were developed with using animation and simulation for students understanding of the phenomena with a particle view point. Many phenomena in a solution were not simplified by colligative property of solution, but tried to explain by the concept of attraction between solute and solvent molecules. This computer assisted learning materials were developed using Flash 5.0 and Flash 6.0 Action Script. Educational effects of the materials on 10th and 11th grade students represented statistically meaningful increase of concept understanding. Especially the materials were effective to the transition stage or formal stage students in 10th grade and formal stage or the natural science major students in 11th grade.

이 연구에서는 고등학교 화학II 교과서의 ‘용액' 단원에 대한 내용을 입자 수준으로 표현한 컴퓨터 보조 수업자료를 개발하고 그 효과를 고등학교 1학년과 2학년 학생들에게 적용하여 그 효과를 알아보았다. 개발된 내용은 교과서에서 제시한 ‘용액' 단원의 주요 내용으로 용해, 증기압, 끓는점과 어는점의 변화, 삼투현상 등으로 구성되었다. 이 연구에서는 애니메이션과 시뮬레이션을 이용하여 자료를 개발하였다. 이 자료에서는 특히 용액에서 일어나는 현상에 대한 주요 개념을 입자 관점에서 이해할 수 있도록 중점을 두었 다. 용액의 여러 현상들을 용액의 총괄성으로 단순화하지 않고, 용매와 용질 사이의 인력 개념으로 설명하였다. 용액과 관련된 자료의 제작은 플래시 5.0과 플래시 6.0의 Action Script를 이용하였다. 개발한 자료를 고등학교 학생들에게 투입한 결과, 통계적으로 유의미하게 개념 향상을 나타내었으며 특히 고등학교 1학년은 과도기와 형식적 조작기 학생들에게, 그리고 고등학교 2학년의 경우에는 형식적 조작기 학생들과 자연계열 학생들에게서 그 효과가 크게 나타났다.

Keywords

INTRODUCTION

Nickel hydroxide finds application in alkaline batteries as cathode and also in electrochromic device as coloring material.1-4 The material undergoes reversible solid-state redox process involving proton insertion/deinsertion between Ni(OH)2 and NiOOH. It crystallizes in brucite structure involving layers or slabs considered as the main feature Nickel hydroxide has two important modifications namely α-nickel hydroxide and β-nickel hydroxide which are widely studied for more than five decades since they differ in structure and hence electrode properties.

In brief, b-nickel hydroxide, crystallizes in rhombohedral lattice with unit-cell lattice parameters of a=3.12 A° and c=4.605 A°. On the other hand, α-nickel hydroxide is a hydrated compound with chemical formula of Ni(OH)2. 0.75 H2O and crystallizes in similar rhombohedral lattice with unit-cell parameters of a=3.08 A° and c=23.41 A°. The a-form has large interlayer spacing of 7.60 A° arising from its d003 planes, whereas β-form offers layers which are just apart by 4.61 A° arising from d001 planes. Upon oxidation the a-nickel hydroxide converts to γ-nickel oxyhydroxide and β-nickel hydroxide to β-nickel oxyhydroxide. The theoretical specific capacity of α-γ couple is 456 mAhg−1 as compared to 289 mAhg−1 for β-β couple based on 1.6 and 1.0 e−s reversibly exchanged during the redox reactions respectively.5,6 Many research efforts are aimed at synthesizing alkali-stable α-nickel hydroxide since it undergoes easy transformation to β-form in battery electrolyte namely alkali.

There are many works concerning synthesis of stable α-nickel hydroxide phases such as aluminum-substituted α-Ni(OH)2 and demonstrating their electrochemical advantage in reversible charge storage. 7,8 Stabilized α-nickel hydroxide electrodes have been fabricated by electrochemical impregnation as well and proved for its superior electrochemical behavior.9 The electrochemical impregnation method involves cathodic polarization of the depositionsubstrate in nickel nitrate bath which results in excess concentration of hydroxyl ions at the substratesurface due to nitrate-ion reduction and hence precipitation of the nickel hydroxide at local high-pH.

The electrochemical impregnation experiments could be broadly divided into two kinds (i) low current density (~1 mAcm−2) deposition which provides beta-phase and (ii) high current density (>20 mAcm−2) deposition which provides alpha-phases.10 Interestingly electrochemically deposited α-nickel hydroxide differs from chemically synthesized α-nickel hydroxide with respect to general chemical composition mainly arising from the nitrate ions coming from the deposition bath. The electrodeposit consists of positively-charged hydroxy-deficient layers of nickel-hydroxide which are chargecompensated by an equal amount of nitrate-ions incorporated in between the layers.11 Additionally water molecules are also incorporated. The general formula of these electrodeposited α-nickel hydroxides are given by Ni(OH)2-x(NO3)x·yH2O where x and y are the amount of nitrate ions and water molecules incorporated in the structure.

In this manuscript we have carried out careful synthesis of electrodeposits in the middle-range of small current densities on nickel and platinum substrates. The structural features of the samples inform the phases to be predominantly alpha-type but with difference in the amount of nitrate incorporation. In turn this nitrate incorporation produces some interesting structural results, which are expected to provide more understanding towards anion-substituted hydroxides. The results are interesting in terms of interlayer distances and faradaic efficiency of the material synthesis.

 

EXPERIMENTAL SECTION

Electro-deposition of nickel hydroxide samples was carried out in open air atmosphere on platinum and nickel substrates by cathodic electrolysis of 0.1 M Ni(NO3)2 solutions prepared from conductivity water (Millipore). In a typical electro synthesis experiment a nickel plate of geometric area, 40 cm2 (both sides) was cleaned and dried to be used as a working electrode substrate. The substrate and a platinum-plate counter electrode were immersed in a stirred solution of 750 ml of 0.1M Ni(NO3)2 (pH=4.69) maintained at 30.00 ℃ by temperature controller (Julabo-Model-FP40). Subsequent to one minute after immersion, the substrate was cathodicaly polarized by passing a galvanostatic current of 40 mA for 10 hours i.e. a charge of 400 mAh with the aid of computer controlled multichannel potentiostat-galvanostat (VMP2- Princeton applied Research). The stirring and temperature control were well maintained during the course of the entire experiment. Immediately after the end of the experiment, the substrate which turned transparent-crystalline green in appearance due to the reasonably-adherent deposit was removed from the electrolyte solution and repeatedly washed with conductivity water for several times. Then the green deposit was removed by dry air at 40 ℃. The collected green powder was dried for 24 hours at 65 ℃ in hot-air-oven and the samples were weighed accurately to calculate the yield and faradaic efficiency.

Further electro-synthesis experiments were carried out in fresh Ni(NO3)2 solutions under similar conditions with currents of 200 mA, 240 mA, 280 mA and 400 mA for 2 h, 1.6 hr, 1.26 hr and 1 hour respectively thus maintaining the total charge of 400 mAh. Thus the current densities of the electrodeposition experiments were 1.0, 5.0, 6.0, 7.0 and 10.0 mAcm−2. Another set of similar experiments were carried out with platinum plate as substrate with the remaining parameters unaltered. Thus 10-samples were systematically prepared for this study(Table 1).

Table 1.Experimental conditions employed for the electrodeposition, amount (mass) of the deposit and calculated faradaic efficiencies of the α-nickel hydroxide samples. In all the experiments the total charge passed is equal to 400 mAh.

The samples were adhered to silver paste and dried for electrical contact to observe SEM pictures. Elemental analysis (EDAX) of the samples was performed in Hitachi scanning electron microscope (SEM S-4200). The experiments were mainly aimed at finding out the percentage content of carbon arising from carbonate ions.

Infra red spectral data of the nickel hydroxide samples were collected at 25 ℃ in FTIR spectrometer (Nicolet Instruments Corporation) provided with data analysis software (Ominc-3.1). Portemer et. al. have suggested the usage of CsI instead of conventionally used KBr as dispersion medium to reduce the loss of IR signal intensity and resolution with regard to nitrate ion. In the present experiments, the samples for the IR spectroscopy experiments consisted of pressed circular pellets. A typical circular pellet was prepared by mixing and grinding 4 mg of nickel hydroxide and 196 mg of CsI followed by compaction at 4 tons load for 10 seconds. The resulting pellet possessed the dimensions of 12.86 mm diameter and 0.85 mm thickness with the IR exposure area being the 0.6 cm2 around the center. Identical pellets were prepared for all the 10-samples for effective comparison.

X-ray diffraction experiments were carried out in Rigaku-Japan diffractometer (Model D/max, Rint 2000) with Cu-K-Alpha radiation (wave length=1.5418 A) as source at a scan rate of 1 deg / min in the twotheta range 5°–70°. TGA and DSC data were col-lected at the scan rate of 5 ℃ per min in TA instrument, USA (model: DSC 2920 and TGA 2050).

Temperature programmed desorption (TPD) studies were carried out in the gas chromatography instrument coupled with mass spectrometer (GC-MS) analyzer connected to the sample holder.12 In a typical experiment 100 mg of the sample was introduced into the bottom of the U-shaped sample tube which was heated by a furnace and the temperature of the sample was measured accurately with the help of a Pt-Rd thermocouple. Helium at a pressure of 6.5 psi was used as the carrier gas to carry the desorbed species at instant of time. The temperature of the GC column was maintained at 250 deg C for fast and effective movement of the desorbed species towards the MS analyzer. The sample was preheated and degassed for 1 hour at 65 deg C and the temperature was increased at the rate of 5° per minute up to 700 ℃. At regular intervals of time (and hence temperature) the desorbed species were detected by the mass spectral analyzer which results in the ion-spectrum which is the plot of ion-current vs temperature. Details regarding desorbed species at each temperature were obtained by deconvolution of the ion-spectrum from the knowledge expected species of known mass numbers. The amount of such species desorbed from the sample over the temperature range 65-700 ℃ was obtained as a graph and it is called the individual species spectrum. The amount of each species in unit mass of the sample is quantified by integrating the individual species spectrum over the entire temperature range. Additionally, if the same species is desorbed at more than one instance they can be individually integrated over the short temperature range to understand the source of the species. This would be more clearly understood with a representative example in the results and discussion section.

The attempts to synthesize CO32− (carbonate-free) samples failed due to the extreme difficulty faced in the production of CO2-free water. Although experimental reports are suggesting the preparation of CO2-free water by purging argon, we found the method not be satisfactisfactory as our synthesis can include CO32− ions even when present in ppm levels. In future these expements could be planned with such conditions.

 

RESULTS AND DISCUSSION

All the electro-deposits were reasonably adherent and crystalline green in appearance, which got detached by drying at 40 ℃, which suggests the absence of any chemical bonding between the sam-ple and substrate. The mass of the nickel hydroxide deposit obtained for a constant input charge of 400 mAh over nickel and platinum substrates for various current densities are tabulated in Table 1. The calculated faradaic efficiencies will be understood upon reading the later section of the article.

Fig. 1.TGA data of Ni(OH)2-x-y(CO3)x/2(NO3)y.zH2O samples electrodeposited at a current density of 6.0 mA cm−2 on (a) platinum substrate and (b) nickel substrate. (↑ refers to upward curvature and ↓ refers to downward curvature and • refers to midpoint).

Fig. 2.FTIR spectra of the electrodeposited Ni(OH)2-x-y (CO3)x/2(NO3)y.zH2O samples (a) on platinum at 5 mAcm−2 (resulted in x-value = 0.1332) and (b) on nickel at 1 mAcm−2 (resulted in x-value = 0.2022).

The elemental analyses show the samples to consist of nickel, oxygen, hydrogen carbon and nitrogen. This suggests that the samples must contain carbonate and nitrate. The elucidation of the anions will be the main study of this manuscript. The TGA data of two representative samples are shown in Fig. 1. But the curves do not show clear and differentiable steps to determine the composition.

The infrared spectral data of two samples as typical examples are shown in Fig. 2. The spectra of all the ten samples studied are similar over the entire infrared range except for the broad band region around 3500 cm−1. In general the spectra show the following absorption signals provided along with the assignments: The signals at 465 cm−1 due to (stretching vibrational modes) γ(NiO), 664 cm–1 for (bending vibrational modes) δ(OH) 1632 cm−1 due to δ(H2O) are assigned unambiguously.12

The presence of carbonate ions are confirmed from the signal at 1048 cm–1 arising due to g(CO32− ) with c2v symmetry and the strong signal at 1365 cm−1 due to the carbonate g(CO32− ). The appearance of signal at 833, 992 and 1482 cm−1 agrees with carbonate as well as nitrate ions in d3h and c2v symmetry. The signals appearing the in the range 3500-3600 cm−1 which are responsible for the OH stretching vibrations under various situations are very interesting and will be discussed towards the end of this manuscript.

The X-ray diffraction patterns of the samples are shown in Figs. 3 and 4. From a broad appearance all the samples look to crystallize in similar α-nickel hydroxide structure. The asymmetry of the higher angle peaks shows additional proof for the formation of turbostratic structures peculiar to α-nickel hydroxide.13 But, when closely analyzed the corresponding 003 lines are shifted to higher angles upon increase in current density which is very prominent in samples deposited on nickel substrate than those deposited on platinum substrate as shown in Figs. 3 and 4. The 003 lines arise from the layers of nickel hydroxide perpendicular to the c-axis of the lattice and hence it is a measure of the interlayer spacing. The XRD patterns were accurately indexed to obtain the lattice parameters of hexagonal unit cell of α-nickel hydroxide. The lattice parameters of all the samples are listed in Table 2. From the lattice constants provided in Table 2 and a view at the diffraction patterns it is clear that lattice expansion occurs for the materials deposited at higher current densities with retention of similar structure. Although the broad peaks indicate smaller crystallite size, reliable values of sizes could not be obtained by debye-sherrer formula due to turbostraticity. Roughly we describe the sample to consist of positively charged hydroxyl deficient nickel hydroxide layers with the charge balanced by the anions in between the layers namely carbonates and nitrates. In turn the amount of these anions change the interlayer distances. The factors responsible for the change in interlayer spacing will be understood with the aid of the chemical composition determined with thermal analysis. The a-lattice parameter remains unchanged around 3.1 A° for all the samples. The c-lattice parameter increases with current density for sample deposited on nickelsubstrate, while as such an effect is not observed for samples deposited on platinum substrate.

Fig. 3.Powder XRD patterns of Ni(OH)2-x-y(CO3)x/2(NO3)y.zH2O electrodeposited deposited on platinum substrate at current densities of (a) 1.0 mA cm−2, (b) 5.0 mA cm−2, (c) 6.0 mA cm−2, (d) 7.0 mA cm−2, (e) 10.0 mA cm−2. The inset shows the peak positions of 003 reflections.

Fig. 4.Powder XRD patterns of Ni(OH)2-x-y(CO3)x/2(NO3)y.zH2O samples deposited on nickel substrate at current densities of (a) 1.0 mA cm−2, (b) 5.0 mA cm−2, (c) 6.0 mA cm−2, (d) 7.0 mA cm−2, (e) 10.0 mA cm−2. The inset shows the peak positions of 003 reflections.

Table 2.The Unit cell parameters and stoichiometry of the electrodeposited Ni(OH)2-x(NO3)x·y H2O samples obtained on platinum and nickel substrates at various current densities.

Apart from the increase change in the c-lattice parameter, it is noteworthy to point out that some samples such as pt-10, pt-05, Ni-10, Ni-07 show very large c-lattice constant values around 27-28 Angstroms which equates to an interlayer (interlamellar) distance of ~9.4 A°. A similar observation with regard to high lattice interlayer distance has been observed by Ismail et al.14 They observed a interlayer distance of 9.3 A° corresponding to the 001 reflection of malice acid intercalated Co(OH)2 phase. But that phase is β-Co(OH)2 with interlayer distance corresponding to c-lattice parameter. This is the one noteworthy reference with respect to high interlayer spacing. This is a first time observation and is unexpected as the usual interlayer distances are around 7.5 A° with the intercalated anions being nitrates. We suspected the large interlayer distance could possibly arise from carbonate ions and nitrate ions present in large numbers and sitting in special configurations. In order to understand this point we have performed a temperature programmed GC-MS experiments.

Fig. 5.Temperature programmed Desorption (TPD) data of Ni(OH)2-x-y(CO3)x/2(NO3)y.zH2O sample deposited on nickel substrate at current densities of 5.0 mA cm−2. The ion-count represents the ion-current signal obtained at each temperature from the mass spectrometer.

The temperature programmed GC-MS experiments yield the ion spectrum and from them individual species spectrum could be obtained. A typical ionspectrum of a sample is shown in Fig. 5. The figure shows the sample to consist of huge amount of desorbable specie. In detail, the peak signal values are 11 million at 137 deg C, 36 million at 273 deg C, 10 million at 336 and 10.7 million at 380 ℃. The sample becomes thermally stable beyond 520℃. Since the sample is supposed to be hydroxy deficient nickel hydroxides, all thermally desorbable species get removed and the sample gets converted to nickel oxide at 520 ℃. We are more interested in the analyzing the spectrum up to 500 ℃ since we plan to investigate the nature and magnitude of the desorbable species and their source.

Fig. 6.Individual-species TPD spectrum for the Ni(OH)2-x-y (CO3)x/2(NO3)y.zH2O sample deposited on nickel substrate at current densities of 5.0 mA cm−2. The data is obtained by the deconvolution of the data presented in Fig. 4.

Since the preliminary investigation such as IR and XRD show the samples to consist of carbonate and nitrate ions intercalated in the nickel hydroxide, the molecular ions arising from four species namely H2O, CO2, NO2 and O2 could be expected to be the cause for the total ion-spectrum. This is also confirmed from the MS spectra result which suggests molecular ions with mass numbers 18, 44, 46 and 32 are only produced and they result from H2O, CO2, NO2 and O2 respectively. Fig. 6 presents the data consisting of four deconvoluted indivual species spectra.

The following processes are responsible for the production of afore mentioned sepecies of desorption:

The data shows that major contribution of ioncurrent arises from the carbonate ions present in the sample followed by H2O molecules then followed by nitrate ions. Contrary to the usual description of alpha-nickel hydroxide samples these samples are found to consist of carbonate ions in excess as compared to nitrate ions. So far in the literature the presence of carbonate ions is neglected and we would like to add this new finding for the future references. With regard to the nature of the carbonate ion, they are released at temperatures of 125 and 280 ℃ with a majority coming from 280 ℃. The nitrate ions are present in small amount as compared to carbonate ions but they are released at higher temperature. This shows that the nitrate ions are more strongly bonded to the lattice than carbonate ions as shown by the desorption temperature.

The amount of CO32−, NO3− and H2O molecules are calculated from the integral area of the individual-species spectra. These integral values were further processes to the get the x, y and z of the formula unit of Ni(OH)2-x-y(CO3)x/2(NO3)y.zH2O. The samples consisted of large but unvarying x value and unvarying z value. But the “y” value i.e. the nitrate content changes in a special fashion over the samples. A plot of the nitrate ion-content vs. the lattice constant obtained for various samples is presented in Fig. 7. It is observed from the figures the interlayer spacing increases with the decreasing content of nitrate ions. The influence of carbonate ions towards the change in lattice constant is minimum as it is present is large excess (30 million). Whereas the nitrate ions are present is small amount (10 million) and their halving causes a significant increase in the lattice spacing although the carbonate ions is present in excess. The formula of these phases are correctly given by Ni(OH)2-x-y(CO3)x/2(NO3)y.zH2O. We could consider the fundamental phase to be Ni(OH)2-x(CO3)x/2.zH2O and the nitrate substitution to result in double-anion substituted phases. The study of purely single anion substituted phases are difficult due to experimental problems arising out of (i) preparation of ultra pure CO2- free water which could result in Ni(OH)2-y(NO3)y.zH2O phases and (ii) availability of suitable electrochemical methods to form Ni(OH)2-x(CO3)x/2.zH2O phases. Carbonate ions are incorporated during the chemical precipitation reaction solution consisting nickel and aluminium nitrate and alkali producing Ni1-xAlx(OH)2\(CO3)x/2.zH2O type of phases.8 The experiments to synthesize such ordered phases are under progress.

Fig. 7.The variation of interlayer spacing with the y-value of the chemical formula, Ni(OH)2-x-y(CO3)x/2(NO3)y·zH2O.

We quantify the above observed lattice contraction of interlayer contraction by the nitrate ions by the couloumbic attraction between interlayer-anions and the positively charged hydroxyl deficient slabs. Similar observation was made by Rhee and Kang in Mg-Al-layered double hydroxides with carbonate ions as intercalated anions. They observed interlayer spacing of 7.90, 7.82 and 7.65 A° for carbonate ion contents (x values) of 0.196, 0.250 and 0.326 in Mg1-xAlx(OH)2(CO3)x/2 phases15. But the between those results and ours are the ions responsible for the coulumbic effect, viz, nitrates are responsible in the anion-substituted α-nickel hydroxide phases as against carbonates in the Mg-Al-LDH phases. In the light of these above findings by the GC-MS experiments which give a clear picture of the nature of anions and their amount would explain the lattice contraction effect. It is felt unnecessary to discuss the results of the TGA data as the discussion involves several predictions when weight loss steps merge as in the case of present samples.

The electrostatic force between the positively charged slab and intercalant could be expressed by the following expression:

where “y” refers to the partial ionic charge of the positively charged slab which is also equal to the total anionic charge. For small variation in the amount of intercalated anions the change in columbic force could be considered negligible and the above expression reduces to an easy form,

A plot of the amount of intercalated nitrate ions per mole vs. inter layer spacing is provided in Fig. 7. The plot is a straight line with a negative slope and it confirms the hypothesis that excess anions bring the positively charged slabs closer. Moreover the effect is brought only by nitrate ions and not carbonate ions although carbonate ions are present is large excess. A possible explanation for this effect could be the tightly bonded nature of nitrate ions as observed from higher desorption temperature in the GC-MS data.

The lattice contraction effect is further augmented by the FTIR signals arising out of the OH stretching vibrations in the range 3500-3600 cm−1 for the hydroxyl groups of nickel-hydroxide slabs. A family of FTIR curves in the range 3500-3600 cm−1 for all the samples arranged according to increasing amounts of nitrate ions is provided in Fig. 8. The samples with larger content of nitrate ions show a smooth broad band and asymmetric band centered around 3560 cm–1 whereas the samples with smaller content of nitrate ions show an additional sharp peak around 3640 cm−1. Indeed the 3640 cm−1 signal becomes less and less visible for samples with high nitrate ions contents. In literature the band around 3560 cm−1 is attributed to stretching vibration of OH group hydrogen bonded to nitrate ions where as the band at 3640 cm−1 is attributed to stretching vibration of free OH groups. The samples with higher nitrate ions have only 3560 cm−1 signal indicating all the OH bonds are strongly associated with nitrate ions through hydrogen bonds, which could be either the cause for lattice contraction or result of lattice contraction. An exact reverse behavior is observed in the samples with lower content of nitrate ions, where free OH IR signal is observed which indicates that interlayer spacing is large enough to allow some of the OH groups to be free. A gradation in lattice contraction results in the diminishing existence of free OH groups.

Fig. 8.FTIR spectra of the Ni(OH)2-x-y(CO3)x/2(NO3)y.zH2O samples arranged in the increasing order of “x” values from (a) to (j) with sample and “y” values as follows: (a) Pt-05; y=0.1332, (b) Pt-10; y=0.1363, (c) Pt-06; y=0.1454, (d) Ni-10; y=0.1480, (e) Ni-07; y=0.1532, (f) Pt-07; y=0.1559, (g) Pt-01; y=0.1675, (h) Ni-06; y=0.1715, (i) Ni-05; y=0.1725 and (j) Ni-01; y=0.2022.

Fig. 9.Effect of electrodeposition current density on results of the Ni(OH)2-x-y(CO3)x/2(NO3)y.zH2O samples in their (a) “a” lattice parameter, (b) “c” lattice parameter, (c) “x” value of the chemical formula, (d) “y” value of the chemical formula and (e) faradaic efficiency of synthesis. Note: Filled-symbols for samples deposited on platinum and open-symbols for samples deposited on nickel substrate.

Fig. 10.Schematic representation of (a) Pt05 i.e., Ni(OH)2-x-y (CO3)x/2(NO3)y.zH2O (y=0.1322) and (b) Ni01 i.e., Ni(OH)2-x-y(CO3)x/2(NO3)y.zH2O (y=0.2022) showing the lattice contraction of hydroxy deficient layers by anions.

Fig. 8 shows an increase in faradaic efficiency with applied current density for both platinum and nickel substrates in a similar trend from 1 to 10 mAcm−2. A mathematical model for the galvanostatic deposition of nickel hydroxide is proposed by Weidner et. al..16 In that work, the efficiency of electrodeposition is well explained with respect to change of current density. Several electrochemical as well as chemical reactions were considered as part of the beginning building blocks, but the weight of nickel hydroxide deposit, which leads to calculation of faradaic efficiency depends on the following reactions:

It is clear from the above chemical equations that the concentration of OH− ions decides the amount of deposit. From these considerations a final expression was derived for the weight of nickel hydroxide deposited as:

where, i is the applied current density, WNi(OH)2 is the molecular weight of the deposit, εOH- efficiency of utilization of OH− ions, A is the geometric area and F is the faraday constant. It is very much expected from expression (6) that the faradaic efficiency which is the ratio of actual weight to the expected weight is directly proportional to the current density and hence the observed behavior of increase in faradaic efficiency with current density is well understood. Mechanistic studies are still in progress to reason out the superior faradaic efficiency of platinum over nickel substrates.

 

CONCLUSIONS

In this study it is demonstrated that an interesting effect is produced in the interlayer spacing for α-nickel hydroxide upon varying the electrodeposition current density close to 5.0 mAcm−2. The response of platinum substrate towards a small change in current density is very prominent in producing a change in interlayer spacing of alpha nickel hydroxide. We have demonstrated that the nature of nitrate ion and hence its amount is the deciding factor in bringing lattice contraction through its columbic attractive force upon the adjacent positively charged hydroxydeficient slabs. In the literature the effect of size of ion on the lattice spacings and hence the properties had been demonstrated.17 We hope to look at these interesting aspects in future. The faradaic efficiency of deposition on platinum substrate is marginally higher than nickel substrate which is attributed to some amount of charge consumed for corrosion of nickel substrate. The response of various parameters including faradaic efficiency at the crucial current density of 6.0 mAcm−2 is interesting and it is under further investigation.

GC-MS analysis of the electrodeposited nickel hydroxide samples show that the major proportion anions are carbonate ions and minor proportion comes from nitrate ions. This is a new observation as the samples are usually assumed to be nitrate conGC-MS analysis of the electrodeposited nickel hydroxide samples show that the major proportion anions are carbonate ions and minor proportion comes from nitrate ions. This is a new observation as the samples are usually assumed to be nitrate containing samples. Further the GC-MS experiments clearly demonstrate that the nitrate ions are strongly bonded in between the positively charged layers as compared to the carbonate ions as inferred from the temperature of their elimination. Such a demarcation is not possible with usual TGA analysis.

References

  1. D. Linden (Ed.) Handbook of Batteries, McGraw Hill, New York, 1995
  2. Kumar, V.G.; Shaju, K.M.; Munichandraiah, N.; Shukla, A.K. J. Power Sources, 1998, 76, 106 https://doi.org/10.1016/S0378-7753(98)00113-X
  3. Tessier, C.; Haumesser, P.H.; Bernard, P.; Delmas, C. J. Electrochem. Soc. 1999, 146, 2059 https://doi.org/10.1149/1.1391892
  4. Carpenter, M.K.; Conell, R.S.; Corrigan, D.A. Solar Energy Materials 1987, 16, 333 https://doi.org/10.1016/0165-1633(87)90082-7
  5. Corrigan, D.A.; Knight, S.L. J. Electrochem. Soc. 1989, 136, 613 https://doi.org/10.1149/1.2096697
  6. Singh, D. J. Electrochem. Soc. 1998, 145, 116 https://doi.org/10.1149/1.1838222
  7. Kumar, V.G.; Munichandraiah, N.; Kamath, P.V.; Shukla, A.K. J. Power Sources 1995, 56, 111 https://doi.org/10.1016/0378-7753(95)02212-Y
  8. Kamath, P.V.; Dixit, M.; Indira, L.; Shukla, A.K.; Kumar, V.G.; Munichandraiah, N. J. Electrochem. Soc. 1994, 141, 2956
  9. Dixit, M.; Jayashree, R.S.; Kamath, P.V.; Shukla, A.K.; Kumar, V.G.; Munichandraiah, N. Electrochem. and Solid State Letters, 1999, 2, 170 https://doi.org/10.1149/1.1390772
  10. Jayashree.R.S.; Kamath, P.V. J. Applied Electrochem. 1999, 29, 449 https://doi.org/10.1023/A:1003493711239
  11. Portemer, F.; Delahaye-Vidal, A.; Figlarz, M. J. Electrochem. Soc. 1992, 139, 671 https://doi.org/10.1149/1.2069283
  12. Jung, K.T.; Kim, W.B.; Rhee C.H.; Lee, J.S. Chem. Mater. 2004, 16, 307 https://doi.org/10.1021/cm030395w
  13. Genin, P.; Delahaye-Vidal, A.; Portemer, F.; Tekaia-Elhsissen, K.; Figlarz, M. Eur. J. Solid State Inorg. Chem. 1991, 28, 505
  14. J. Ismail, M.F. Ahmed, P.V. Kamath, G.N.Subbanna, S. Uma and J. Gopalakrishnan J. Solid State Chem. 1995, 114, 550 https://doi.org/10.1006/jssc.1995.1084
  15. Rhee, S.W.; Kang, M.J. Korean J. Chem. Eng. 2002, 19, 653 https://doi.org/10.1007/BF02699312
  16. Murthy, M.; Nagarajan, G.S.; Weidner, J,W.; VanZee, J.W. J. Electrochem. Soc. 1996, 143, 2319 https://doi.org/10.1149/1.1837000
  17. Taibi, M.; Ammar, S.; Jouini, N.;, Fievet, F.; Molinie, P.; Drillon, M. J. Mater. Chem. 2002, 12, 3238 https://doi.org/10.1039/b204087e

Cited by

  1. Nanostructured nickel oxide ultrafine nanoparticles: Synthesis, characterization, and supercapacitive behavior vol.23, 2014, https://doi.org/10.1016/j.mssp.2014.02.027
  2. Electrochemical preparation of α-Ni(OH)2 ultrafine nanoparticles for high-performance supercapacitors vol.18, pp.6, 2014, https://doi.org/10.1007/s10008-014-2381-7