Abstract
The static friction coefficients of 4 samples against each different temperatures were similar values. Compared against RT, at $80^{\circ}C$ the static friction coefficients decreased from 0.130 to 0.116 that was equal from 88% to 90% of the static friction coefficients respectively. Otherwise the dynamic friction coefficients compared against RT, decreased from 0.138 to 0.088 which was from 71% to 77.5% respectively at $80^{\circ}C$. The noise characteristics were judged by s/d value. And when the s/d value was limited less than 0.8, noise concerns were released. At 3000 engaging cycles the static friction and the dynamic friction coefficient were 0.137 and 0.073 respectively. When plate pressure rose up to $195kg_f/cm^2$, the static friction coefficient decreased from 0.137 to 0.125 but this decreasing could be considered as stable. When speed rose up to 2200rpm, the static friction coefficient decrease from 0.14 to 0.13 but this decreasing could be considered as stable. At 3000 engaging cycles the amount of worn out was 0.04 : the thickness of disc was decrease from 4.72mm to 4.68mm. But regarding the normal operation condition, further more worn-out could not be expected. Therefore concerning worn-out, the basic oil could be considered as appropriate.