Acid Pickling Characteristics of Stainless Steel by the Mixed Solution of Hydrochloric acid, Hydrofluoric acid and Hydrogen Peroxide

염산-불산-과산화수소 혼합용액에 의한 스테인레스강의 산세 특성

  • Chun, Heedong (Environmental Research Lab, Research Institute of Industrial Science & Technology) ;
  • Choi, SangGyo (Environmental Research Lab, Research Institute of Industrial Science & Technology)
  • 전희동 ((재)포항산업과학연구원 환경연구실) ;
  • 최상교 ((재)포항산업과학연구원 환경연구실)
  • Received : 2005.01.17
  • Accepted : 2005.02.15
  • Published : 2005.03.01
Download PDF
⟨ Previous Next ⟩

Abstract

Nitric acid free pickling solution was applied to solve the severe environmental problems attributed to nitric acid during pickling process of stainless steel product. In points of pickling capability and erosion of stainless steel base metal, a solution contains I% of hydrochloric acid and 2% of hydrofluoric acid and hydrogen peroxide was revealed as the best alternative to conventional mixed acid of nitric acid and hydrofluoric acid. To keep the pickling capability, it was necessary to maintain the concentration ratio of hydrogen peroxide to hydrochloric acid above 0.5.

스테인레스강의 산세공정에서 사용하는 질산으로 인한 환경문제를 해결하기 위하여 질산을 포함하지 않는 새로운 산세용액을 개발하고자 하였다. 산세용액의 반복 사용 시의 산세성능과 모재의 침식 정도를 기준으로 연구한 결과, 산 1%, 불산 및 과산화수소 각 2% 의 조성을 갖는 용액이 기존의 질산-불산 용액과 유사한 수준의 우수한 산세특성을 나타내었다. 또한 산세능을 유지하기 위해서는 염산 대비 과산화수소의 비율을 0.5 이상 유지해야 하는 것으로 나타났다.