Effects of Physical Properties on Waterborne Polyurethane with Poly(tetramethylene glycol) (PTMG) and Polycaprolactone (PCL) Contents

폴리(테트라메틸렌 글리콜)(PTMG)/폴리카프로락톤)(PCL) 폴리올의 혼합비가 수분산계 폴리우레탄의 물성에 미치는 영향

  • Yang, Yun-Kyu (School of Advanced Material Engineering, College of Engineering, Chungnam National University) ;
  • Kwak, Noh-Seok (School of Advanced Material Engineering, College of Engineering, Chungnam National University) ;
  • Hwang, Taek-Sung (School of Advanced Material Engineering, College of Engineering, Chungnam National University)
  • 양윤규 (충남대학교 공과대학 신소재공학부) ;
  • 곽노석 (충남대학교 공과대학 신소재공학부) ;
  • 황택성 (충남대학교 공과대학 신소재공학부)
  • Published : 2005.01.01

Abstract

In this study, waterborne polyurethanes were synthesized with poly(tetramethylene glycol) (PTMG), polycarprolactone PCL), dimethylol propionic acid (DMPA) and different molar ratio of chain extender. Particle size, polydispersity, thermal and mechanical properties of waterborne polyurethane were investigated. The particle size of waterborne polyurethane was in the range of 5∼200 nm and decreased with increasing the amounts of PCL and chain extender. Glass transition temperatures ($T_g$) were in the range of -70∼-45 ${\circ}C$ and increased with as PCL and chian extender (ED) contents increased. The $T_g$ of polyurethane prepared from the mixture showed similar trends as compared with those of in the same values of synthetic polyurethane using PTMG or PCL, respectively. Also, mechanical properties of mixed polyols (PTMG and PCL) were lower than those of PTMG and PCL, respectively.

본 연구에서는 폴리(테트라메틸렌 글리콜)(PTMG), 폴리카프로락톤(PCL) 및 isophron diisocyanate(IPDI)와 dimethylol propionic acid(DMPA)를 이용하여 물에 분산이 가능한 수분산계 폴리우레탄을 제조하였다. 또한, 사슬연장제의 함량을 변화시키면서 입도분석과 기계적 물성 등을 시험하였다. 유화된 폴리우레탄의 입경은 50~200 nm이었으며, PCL과 사슬연장제의 함량이 많을수록 작아졌으며, $T_g$는 -70~-45 ${\circ}C$ 범위이고 사슬연장제의 함량이 증가함에 따라 $T_g$는 다소 상승하였다. PTMG와 PCL을 혼합하여 합성한 폴리우레탄의 $T_g$는 이들을 각각 사용하여 합성한 $T_g$와 비슷하게 나타났다. 인장강도는 PCL과 사슬연장제의 함량이 증가할수록 높아졌으며 신율은 낮아졌다. 폴리올을 혼합하였을 경우에는 단독으로 합성한 것보다 전반적으로 기계적 물성이 저하되는 것을 확인하였다.

Keywords

References

  1. C. Hepburn, Polyurethane Elastomers, Elsevier, London, 1991
  2. D. Dieterich, Progress in Organic Coatings, 281 (1981)
  3. T. O. Ahn, S. U. Jung, H. M. Jeong, and S. W. Lee, J. Appl. Polym. Sci., 51, 43 (1994)
  4. G. Oertel, Polyuretlwne Handbook, Hanser, New York, p 27 (1985)
  5. J. P. Santerrre and J. L. Brash, J. Appl. Polym. Sci., 52, 515 (1994)
  6. C. H Cho, H. D. Seo, B. H. Min, H. K. Cho, S. T. Noh, H. G. Choi, Y. H. Cho, and J. H. Kim, J. Korean Ind. Eng. Chem., 13, 825 (2002)
  7. Y. Chen and W. C. Chan, Polymer., 29, 1995 (1998) https://doi.org/10.1016/0032-3861(88)90006-7
  8. O. Lorenz and H. Hick, Macromolecules, 72, 115 (1978)
  9. B. K. Kim and T. K. Kim, J. Appl. Polym. Sci., 43, 393 (1991)
  10. R. E. Tieback and P. H. Markusch, J. Coat. Technol., 16, 39 (1986)
  11. H. Aa. AI-Salah, H. X. Xiao, J. A. Malean, and K. C. Frisch, J. Polym. Sci.; Part A: Polym. Chem., 26, 160 (1988)
  12. C. Hepbum, Polyurethane Elastomers, Applied Science Publishers, London and New York, p 50 (1982)
  13. B. P. Thapliyal and R. Chandra, Polym. Int., 24, 7 (1991)
  14. J. H. Sanders and K. C. Frisch, Polyurethanes Chemistry and Technology, Interscience, New York, 1962
  15. D. W. Kang, Y. M. Kim, andD. K. Kweon, Polymer(Korea), 22, 4 (1998)
  16. S. K. Kim, K. S. Kim, T. K. Kim, and G. J. Oh, Elastomer, 35, 281 (2000)
  17. L. Fambri, A. Pegoretti, C. Gavazza. and A. Penati, J. Appl. Polym Sci., 81, 1216 (2001) https://doi.org/10.1002/app.1407
  18. J. B. Ahn, H. K. Cho, C. N. Jeong, and S. T. Noh, J. Korean Ind. Eng. Chem., 8, 2 (1997)
  19. T. Y. Lee, H. S. Lee, and S. W. Seo, Polymer Science and Technology, 10, 597 (1999)