Abstract
Changes of sound absorption capability and anatomical features of wood by delignification treatment was estimated. Sound absorption coefficients of wood and delignificated wood had been measured by the two microphone method and anatomical changes of delignificated wood examined by SEM observation. The sound absorption coefficients of delignificated wood generally seemed to be higher than those of normal specimen. Especially, in the frequency range of 2 to 4 KHz, they was about 50% higher than those of normal specimen. Abundant small cracks generated on the cross sectional surface of delignificated wood and the weight of delignificated wood decreased about 8% than that of normal wood. It was considered that the small cracks formed by delignification treatment behaved as a sound absorbing pore.
목재에 대한 탈리그닌처리에 의한 목재의 흡음성능과 구조적 특징의 변화를 관찰하고자 목재횡단방향으로 채취한 원반형시험편을 탈리그닌처리하여 무 처리 목재와 구조적 특징의 변화를 관찰하고, 흡음율을 측정 비교하였다. 측정주파수범위에서 탈리그닌처리한 시험편이 보통의 시험편보다 높은 흡음율을 나타내었으며, 특히 2~4 KHz의 주파수영역에서는 50% 정도 높은 흡음율을 나타내었다. 또한 탈리그닌처리한 목재는 무 처리 목재보다 중량이 8% 정도 감소하였으며, 탈리그닌처리한 목재의 횡단면에서는 다수의 미세할렬이 발생하여 이들이 흡음공극으로 작용하여 특정주파수영역에서 흡음율이 증가된 것으로 사료된다.