MOD-TFA 공정에 의한 YBCO박막제조시 과잉 yttrium첨가 효과에 관한 연구

Effects of Excess Yttrium Addition on YBCO Thin Films Prepared by TFA-MOD Process

[ $YBa_{2}Cu_{3}O_{7-x}$ ] thin films were fabricated on $LaAlO_3$(100) substrate by TFA-MOD process. Yttrium-excess (0, 2.5, 5, 10, 15, 20 $at\%$) coating solution was prepared by adding extra amount of yttrium into a stoichiometric(Y:Ba:Cu=1:2:3) TFA precursor solution. Results are presented concerning the influence of excess yttrium additions on the microstructure development and superconducting properties of $YBa_{2}Cu_{3}O_{7-x}$ film. Large sized CuO particles was observed by SEM EDS investigation. The addition of excess yttrium affected little on $T_c$ of $YBa_{2}Cu_{3}O_{7-x}$ film. $J_c$ of YBCO film was enhanced with excess yttrium addition. Jc maximum of $2.21\;MA/cm^2$ (77 K, self field) appeared with the $15\;at\%$ addition of excess yttrium. With further yttrium addition up to $20\;at\%$, Jc decreased down to $0.9\;MA/cm^2$.