Abstract
Today the application of antiwashout underwater concrete to the construction sites is increasing steadily, while its reliability is in issue. Particularly, antiwashout underwater concrete is known to have very weak durability on frost attack, and hence Japan society of civil engineers(JSCE) regulated that not to use of antiwashout underwater concrete where the freezing and thawing is suspected. This study aims the improvement of the freezing and thawing resistance for antiwashout underwater concrete. From the results of fundamental test, FA20 and SG50 showed good performance in fluidity and long term compressive strength than control concrete. Meanwhile, MK10 marked the highest compressive strength through the whole curing age but a defect on fluidity was discovered. The results from the repeated freezing and thawing test show that the large volumes of air entrapped by cellulose based antiwashout underwater admixture gave bad effects to frost durability and hence not much benefits were confirmed from the use of mineral admixtures. However there were some increasing effects on frost durability of MK10 and SG50 by securing $6{\pm}0.5\%$ of entraining air. In the meantime, there was a increasing tendency of frost durability by increasing blame's fineness of ground granulated blast furnace slag.
수중불분리성 콘크리트의 적용 사례가 점차 증대되고 있는 추세임에도 불구하고 역사가 짧은 탓으로 신뢰성 등에 대한 문제점을 지적하고 있다 특히 수중불분리성 콘크리트는 동결응해에 대한 저항성이 매우 취약한 것으로 알려져 있어 일본토목학회에서는 동결융해작용을 받는 지역에서는 사용해서는 않된다고 규정하고 있다. 본 연구에서는 수중불분리성 콘크리트의 내구성을 향상시키기 위한 목적으로 광물질혼화재 3종류로 제조한 수중불분리성 콘크리트의 기초물성과 동결응해 저항성에 대한 실험을 실시하였다. 본 연구실험결과 FA20 및 SG50의 유동성 및 장기강도는 기준콘크리트 보다 양호한 경향을 보인 반면 현탁물질량은 약간 큰 값을 나타내었다. 한편 MK10의 경우, 빠른 수화반응으로 현탁물질량과 압축강도는 양호한 결과를 나타내었으나 유동성은 다소 떨어지는 문제점이 있었다. 한편, 수중불분리성 콘크리트의 동결응해 저항성은 셀룰로오스계 수중불분리성 혼화제에 의한 크고 불규칙한 갇힌공기 때문에 광물질혼화재를 혼합한 경우에도 효과가 적었으나 SG50과 MK10의 공기량 $6{\pm}0.5\%$의 경우, 동결응해 저항성이 약간 향상되는 결과를 얻었다. 그러나 고로슬래그 미분말의 분말도를 달리한 경우 분말도가 증가할수록 활성도가 높아져 동결응해 저항성이 향상되는 경향을 나타내었다.