Abstract
The object of this study is to prove the quality and reliability of recycled aggregate concrete by finding a way to improve the durability of the material through the experiment on the accelerated carbonation, freezing and thaw, and drying shrinkage, analysing the influence on the durability to Promote more active use of recycled aggregate concrete. The result of study as follows. (1) Resistibility to the freeze and thaw of the recycled aggregate concrete showed relative dynamic modulus of elasticity over $90\%$ which is very good, and all cycles show $99.2{\~}91.0\%$ dynamic modulus of elasticity which is improved compared with the $97.5{\~}90.6\%$ relative dynamic modulus of elasticity of ordinary concrete made of broken stone. (2) Carbonated thickness of the recycled aggregate concrete and the normal concrete was similar or it appeared with the tendency which it diminishes more or less. (3) Length change rate in drying contraction of the recycled aggregate concrete made of the recycled aggregate was lower than the ordinary concrete made of the broken stone by $18.5{\~}3.9\%$ in all blending.
본 연구는 재생골재 콘크리트의 적극적인 활용을 위하여 재생굵은골재를 대체율에 따라 혼합골재로 하는 재생골재 콘크리트의 동결응해 저항성, 탄산화 저항성 및 건조수축에 대한 시험을 실시하여 내구특성의 영향요인을 분석하고 내구성 증진방안을 강구함으로써 재생골재 콘크리트의 품질과 신뢰성을 확보하는데 그 목적이 있다. 연구결과는 다음과 같다. (1) 재생굵은골재를 혼합골재로 하는 재생골재 콘크리트의 동결융해 저항성은 모든 대체율에서 $90\%$를 상회하는 상대동탄성계수로 나타나 우수한 결과를 보였으며, 전 사이클에서는 $99.2{\~}91.0\%$의 상대동탄성계수의 범위를 보여 쇄석을 사용한 보통 콘크리트의 상대 동탄성계 수 범위인 $97.5{\~}90.6\%$에 비해 향상된 내동해성으로 나타났다. (2) 재생골재 콘크리트의 촉진탄산화 깊이는 대체율이 증가함에 따라 대체하지 않은 보통 콘크리트와 유사하거나 다소 감소하는 경향으로 나타났다. (3) 재생굵은골재를 혼합골재로 하는 재생골재 콘크리트의 건조수축에 의한 길이변화율은 전 배합에서 쇄석을 사용한 보통 콘크리트보다 $18.5{\~}3.9\%$ 작게 나타났다.