Abstract
The clinkerbility and the behaviour of formation of $3CaO{\cdot}Al_{2}O_3$ were studied using the mixture of waste oyster shell and spent oil-refining catalyst mainly by the mineral and microstructural observation. By virtue of the formation of $12CaO{\cdot}7Al_{2}O_3$ at relatively low temperature and its successive reaction with CaO, the $3CaO{\cdot}Al_{2}O_3$ clinkers were formed easily without affection of minor constituents contained in oyster shell. Thus clinkers were formed at $1400^{\circ}C$ directly but began to melt incongruently at higher temperature above that. Aluminium hydroxide, however, was not desirable as an aluminous raw materials of the clinker because rapid melting occurs before $3CaO{\cdot}Al_{2}O_3$ forms main clinker mineral.
[ $3CaO{\cdot}Al_{2}O_3$ ] 클링커 제조 원료로서의 굴 패각과 정유 폐 촉매의 사용 가능성과 이들 조합물의 클링커 소성성 및 광물 생성거동을 광물상과 미구조 관찰을 중심으로 확인하였다. 굴 패각에 함유된 불순물은 클링커의 합성에 영향을 미치지 않았고 이들 조합물은 비교적 저온에서 $12CaO{\cdot}7Al_{2}O_3$를 생성한 후 다시 CaO와의 반응으로 $3CaO{\cdot}Al_{2}O_3$를 생성하므로 $1400^{\circ}C$에서의 1회 소성으로 클링커 합성이 가능하였다. 그 이상의 온도에서는 분해용융이 진행되었으며 동일한 소성 조건에서 알루미나원으로 수산화알루미늄을 사용할 경우에는 $3CaO{\cdot}Al_{2}O_3$의 생성이 완료되기 전에 용융되어 클링커의 합성이 불가능하였다.