High Temperature Drying of Pitch Pine Lumber

리기다소나무 고온건조

The objective of this study was to evaluate the applicability of high temperature drying to pitch pine (Pinus rigida) lumber, especially intended for use as lamina of structural glued laminated timber (glulam), to enhance the efficient utilization and provide added-value to that species. The high temperature schedule and drying procedures utilized were shown to be reasonable for drying glulam lamina due to the occurrence of small moisture gradients, minimal residual drying stress, and low warpage. Through preliminary tests, it was confirmed that residual resin at lamina surfaces did not adversely affect the gluing process. However, quantitative analysis of resin is required for developing a method to constrain the occurrence of pitch trouble with respect to decreasing long-term adhesive and finish durability of glulam in use after manufacturing. The final moisture content of high temperature dried lamina was much lower than target moisture content and discoloration was more severe than anticipated. In a further study, it will be necessary to determine the optimal drying conditions, such as temperature, humidity, drying time, and top load restraint level, which could best control discoloration, warpage, and moisture content of the lamina, while minimizing fuel expense.

본 연구에서는 국산 리기다소나무의 대량 수요 창출과 이용기술 개발, 특히 구조용집성재 라미나로서의 이용 가능성 구명을 위해 고온에서 건조된 판재의 변형량과 변색정도를 조사 평가하였다. 함수율 분포시험을 통해 평가된 고온건조판재 내 적은 함수율 경사, 프롱테스트를 통해 확인된 적은 내부 잔류응력, 집성가공 가능한 적은 변형량 등은 본 연구에서 적용된 고온건조스케쥴이 구조용집성재용 라미나 건조조건으로 사용 가능성이 높다는 결과를 보여주었다. 예비실험을 통해 송진에 의한 접착장애는 발생하지 않는 것으로 확인 되었으나, 잔류수지에 의한 구조용집성재의 접착내구성 및 도장성능 감소현상 구명을 위한 수지정량 분석시험이 추후 요구되었다. 또한 최종 함수율이 집성재 라미나로서 이용 가능한 함수율보다 상당히 낮은 수준으로 건조되었으며 저온열기건조 판재에 비해 변색이 심하므로 함수율 제어 및 변색 억제를 위한 최적의 건조조건 구명에 대한 연구가 좀더 필요할 것으로 사료된다.