A Study on the Development of Corrosion Inhibitor Treating Surface for Reinforcement Concrete Structures

철근 콘크리트 구조물용 표면 처리형 철근 부식억제제의 개발에 관한 연구

When the concrete is subjected to chloride attack or carbonation, the passive steel normally initiate corrosion. By product of corrosion make volume of concrete expand 3 to 8 times and induce the stress which lead cracking and spalling of concrete. It result in the loss of the integrity of the concrete structures. Several corrosion inhibitors imported from America, Japan and Europe are currently being used to repair the concrete structures in Korea. However, questions has been raised for protective effect of the corrosion inhibitors which applied in steel reinforced concrete structures. Therefore, we investigated the influence of type and amount of corrosion inhibitors through the tests immersing in salty water. In addition, we developed the corrosion inhibitive agent treating to surface of concrete structures for improving resistance to penetration and corrosion of the steel reinforcement.

콘크리트는 내구성이 우수하고 경제적이기 때문에 강재와 더불어 건설재료로서 가장 많이 사용되어 왔다. 그러나 최근 들어 여러 연구결과와 현장점검 결과에 의하면 노출환경과 사용재료에 따라 내구성이 저하되어 실제 구조물에 심각한 문제를 일으키는 것으로 조사되고 있다. 우리나라는 삼면이 바다로 이루어져 있어 염해 피해 가능지역이 많을 뿐만 아니라 도시집중화에 따른 배기가스에 의한 중성화 현상이 심하게 발생하고 있다. 즉 염해와 중성화에 의한 철근부식이 발생할 가능성이 어느 나라 못지 않게 높다고 말할 수 있다. 본 연구에서는 먼저 철근부식을 억제 또는 방지 가능한 물질에 대해 철근부식시험을 실시하여 방청효과를 검토하여, 그 결과를 바탕으로 콘크리트로의 침투성능 및 방청성능을 고려하여 도포형 철근부식억제제를 개발하였다.