Resistance of Chloride Penetration into High Strength Concrete Containing Mineral Admixtures according to Curing Conditions

광물질혼화재 혼합 고강도콘크리트의 양생조건에 따른 염화물이온 침투저항성

In recent years, construction company makes inroads into the world construction market, and receives the order of extra-large concrete structure under marine environment in south-east asia specially. At this point of time, to enhance the quality of concrete, we research the High Strength Concrete (HSC) containing mineral admixtures. In this study, therefore, HSC with various combination of ordinary portland cement(OPC), blast-furnace slag(SG), silica fume(SF), and expansion admixture(SS) are cured 23 and $35^{\circ}C$ considering the site weather, and are cured in water for 3, 7 or 56 days respectively. Test results show that the HSC cured at $35^{\circ}C$ gains higher early-age strength but eventually gains lower later-age strength compare with the HSC cured at $23^{\circ}C$. Especially, HSC with combination of OPC+SG+SF+SS or OPC+SG+SF show very excellent resistance of chloride penetration. The permeability of HSC was therefore enhanced as because of containing the proper content of SG, SF, and SS and making dense micro-structure of HSC.

근년에 와서 우리나라 건설업체의 해외진출이 빈번해 지고 있는 시점에서 특히 동남아 지역에서 대형 해양콘크리트구조물 등의 수주물량이 크게 증가하고 있는 추세를 감안하여 콘크리트 품질향상의 일환으로 광물질혼화재를 혼합한 고강도콘크리트에 착안하게 되었다. 그래서 광물질혼화재의 혼합률을 각각 달리하여 현장의 기후조건을 고려한 양생온도 $23^{\circ}C$ 및 $35^{\circ}C$의 2 종류와 양생조건을 3 종류로 변화시킨 4 배합, 16종류의 고강도콘크리트를 제조하였다. 본 연구 결과, 광물질혼화재를 혼합한 고강도콘크리트를 $35^{\circ}C$로 양생한 경우 초기재령에서 압축강도가 $23^{\circ}C$로 양생한 경우보다 컸으나 재령 28일 이후에는 반전되었다. 특히 고로슬래그미분말, 실리카흄과 팽창재 혼합 및 고로슬래그미분말과 실리카흄을 혼합한 고강도콘크리트의 총통과전하량은 각각 Negligible 및 Very low에 해당되는 매우 좋은 결과를 나타내었다. 따라서 고로슬래그미분말, 실리카흄 및 팽창재를 각각 적정량 혼합함에 따라 밀실한 고강도콘크리트의 제조가 가능하게 됨으로써 염화물이온 침투저항성이 크게 향상되었다.