Development of Organic Paste Porcelain for Fixed Prostheses
유기조성물을 이용한 페이스트형 일반도재 시스템
-
Han, Jung-Suk
(Department of Prosthodontics, College of Dentistry, Seoul National University) ;
-
Lee, Myung-Hyun
(Next Generation Enterprise Group, Korea Institute of Ceramic Engineering & Technology) ;
- Kim, Dae-Hyun (Jeil Dental Laboratory) ;
- Chung, Hun-Young (Department of Prosthodontics, College of Dentistry, Seoul National University)
- Published : 2004.12.30
Abstract
INTRODUCTION: The build-up method has been used for application of porcelain powder on the metal framework to make final tooth shape conventionally. This method takes time and need skill to mimic final shade and shape of porcelain fused to metal crown. The purpose of this study was to develop standard shape and shade laminating porcelain forms to reduce build-up time. METHODS: To make tooth form porcelain paste, several liquid organic compounds were added to conventional feldspathic porcelain. The amount of additives and rheologic property were tested to find out best composition. Comparison of mixing methods to reduced porosity, proper heating schedule, and measurement of shrinkage amount and residual organic materials were performed to set-up standard procedures. Finally, biaxial flexural strength and color of preformed laminated paste porcelain were compared with those of porcelain which fabricated by the conventional build-up method. RESULTS: There was no significant difference in physical properties and color stability between two fabrication methods after various testing methods. Conclusion: This new build-up method can be applied to fabricate the PFM crown and bridge without any loss of strength and optical properties.
덴틴, 에나멜, 투명 일반도재를 페이스트화 하여 치아의 색상, 투명도 및 구조를 고려한 복합층구성물을 미리 제조하여 심미수복물을 용이하게 제작하는 공정을 개발하였다. 페이스트 상태에서 성형성과 유동특성이 확보되고, 소성 후 색도, 및 강도 등의 제특성들을 만족시킬 수 있는 결합제 시스템으로서 UV (creation universal liquid)를 선정하였고 조성 및 최적화가 이루어졌다. 페이스트는 24시간까지도 점성 및 작업성이 유지되었고, 이를 이용하여 복합층 구성물의 용이한 성형이 가능하였다. 소성수축률은 15.2%로 기존의 방법으로 제조한 시편에 비해 0.8% 낮았으나 유의차는 없었다. spectrophotometer에 의한 색도특성 관찰결과 덴틴재를 기존 제조방식으로 제조한 시편과 페이스트형 도재 시스템으로 제조한 시편에서