Shot-peening 표면처리된 Ti 함유 스테인리스강의 응력균열부식

Stress Corrosion Cracking Characteristics of Shot-peened Stainless Steel Containing Ti

  • 최한철 (조선대학교 치과대학 치과재료학교실 및 생체재료나노계면활성화센터)
  • 발행 : 2004.12.01
PDF 다운로드
⟨ 이전 논문 다음 논문 ⟩

초록

Stress corrosion cracking(SCC) characteristics of shot-peened stainless steel containing Ti (0.09 wt%-0.92 wt%) fabricated by the vacuum furnace were investigated using SCC tester and potentiostat. The homogenization and the sensitization treatment were carried out at $1050^{\circ}C$ for 1hr and $650^{\circ}C$ for 5 hr. The samples for SCC were shot-peened using $\Phi$0.6 mm steel ball for 4 min and 10 min. Intergranular and pitting corrosion characteristics were investigated by using EPR and CPPT. SCC test was carried out at the condition of$ 288^{\circ}C$, 90 kgf pressure, water with 8 ppm dissolved oxygen, and $8.3xl0^{-7}$/s strain rate. After the corrosion and see test, the surface of the tested specimen was observed by the optical microscope, TEM and SEM. Specimen with Ti/C ratio of 6.14 showed high tensile strength at the sensitization treatment. The tensile strength decreased with the increase of the Ti/C ratio. Pitting and intergranular corrosion resistance increased with the increase of Ti/C ratio. Stress corrosion cracking strength of shot-peened specimen was higher than that of non shot- peened specimen. Stress corrosion cracking strength decreased with the increase of the Ti/C ratio.

키워드

참고문헌

  1. Norio Nagata, 'Enviromentally Assisted Cracking of Structural Materials for Light Water Reactors', NRIM, Japan, (1994) 2
  2. E. C. Bain, R. H. Aborn, J. J. B. Rutherford, Trans. Amer. Soc. Steel Treat., 21 (1933) 481
  3. S. Bamartt, D. Van Rooyzn, J. Electrochem, Soc., 109 (1962) 343 https://doi.org/10.1149/1.2425416
  4. S. Szklarska-Smialowska, G. Cragnolino, Corros., 36 (1980) 653 https://doi.org/10.5006/0010-9312-36.12.653
  5. A. J. Sedriks, 'Corrosion of Stainless Steels', John Wiely & Sons Inc., New York, 1979
  6. Sohan Lal, G.S.Upadhyaya, J. Mater. Sci., 24 (1989) 3069 https://doi.org/10.1007/BF01139020
  7. J. J. Daly, D. E. Johnson, Adv. Mater. Pocess., 137 (1990) 49
  8. 최한철, 김관휴, 대한금속학회지., 35 (1997) 338
  9. H. Werner et al., Korrosion (Germany), 22 (1991) 175
  10. W. T. Tsai et al., Corrosion, 50 (1994) 98 https://doi.org/10.5006/1.3293507
  11. Tomoya Kato et al., Zairyo-to-Kankyo, 46 (1997) 305 https://doi.org/10.3323/jcorr1991.46.305
  12. D. Peckner, Hand Book of Stainless Steels, McGrawHill Book Co., 1977
  13. Vladimir Cihal: 'Intergranular Corrosion of Steels and Alloys', Elsevier, NY, 1984. p.138
  14. M. Pourbaix, 'Atlas of Electrochemical Equilibria in Aqueous Solutions', Pergamon Press, p.213, New York, 1966
  15. Bo Rosberg, Anders Rosengren, 'Slow Starain Rate Testing in High-Purity Water at Controlled Electrode Potential' , Laboratory Corrosion Test and Standards,ASTM STP 866 (1983) 427
  16. W. T. Tsai et al., Corrosion, 50 (1994) 98 https://doi.org/10.5006/1.3293507