In this study, treatment conditions for monazite concentrate in Hong-Cheon area deposit were studied with NaOH fritting decomposition and HCl leaching experiments. At condition of NaOH fritting decomposition, it was appropriate to adopt particle size of -200 mesh monazite, reaction temperature of about $460^{\circ}C$ and NaOH/TREO mole ratio of 6. In case of HCl leaching for decomposed product, it was appropriate to use hydrochloric acid of above 8N with leaching temperature of above $80^{\circ}C$, leaching time of 2 hrs and pulp density of about 10%. A rate of decomposition and leaching for monazite was above 90% under optimum conditions. Sodium phosphate compound was effectively recovered from NaOH decomposed solution, and mixed rare earth chloride solution was prepared with HCl leaching of decomposed product.
본 연구에서는 국내 홍천산 모나자이트 정광의 가성소다 분해 및 분해산물의 염산 침출에 대한 처리조건을 확립하고자 하였다. 분해 반응의 조건은 입자크기의 -200 mesh 이하이면 적절하였고, 반응온도 $460^{\circ}C$부근에서 원활한 분해가 이루어 졌으며, 가성소다 첨가량은 NaOH/TREO mole ratio 6정도가 효과적이다. 또한 침출반응의 조건은 염산농도 8N 및 반응온도 $80^{\circ}C$이상이 침출에 적절하였으며, 반응시간 2시간 및 광액 농도 10%가 효과적이다. 그리고 최적조건하에서 모나자이트의 분해 침출율은 90%이상이였고, 부산물 형태로 인산소다 화합물은 효과적으로 회수하였으며, 희토류 원소별 분리에 적합한 시료용액을 조제하였다.