Behavioral Characteristics of Fatigue Cracks in Small Hole Defects Located on Opposite Sides of the Shaft Cross Section

  • Sam-Hong (Department of Mechanical Engineering, Korea University) ;
  • Il-Hyuk (Department of Mechanical Engineering, Graduate School, Korea University) ;
  • Jeong-Moo (Research Institute of Engineering & Technology, Korea University)
  • 발행 : 2004.10.01
PDF 다운로드
⟨ 이전 논문 다음 논문 ⟩

초록

The shaft with the circular cross section has symmetric structural combination parts to keep the rotating balance. Hence the crack usually initiates from symmetric combination parts due to the stress concentration of these parts. In this study to estimate the fatigue behavior of symmetric cracks, the fatigue test was performed by using a rotary bending tester and the specimen with symmetric defects in circular cross section. The characteristics of crack initiation and propagation on the symmetric surface cracks in circular cross section were examined. We also observed the internal crack using the oxidation coloring method and investigated the fatigue behavior using the relationship between the surface crack and the internal crack. As a result, the fatigue life of symmetric cracks was reduced by 35% compared to that of a single crack. We examined the characteristics of fatigue behavior of elements with symmetric cracks using internal crack propagation rate and maximum stress intensity factor range that were obtained from an approximation method.

키워드

참고문헌

  1. Song, S. H. and Oh, H. S., 'Behavior of Initiation and Propagation of Fatigue Cracks around Micro Holes,' Journal of the Korea Committee for Ocean Research and Engineering, Vol. 1, No.2, pp. 250-258, 1987
  2. Endo, M. and Murakami, Y., 'Effects of Artificial Small Defect on Torsional Fatigue Strength of Steel,' Trans. ASME, Vol. 109, pp. 124-129, 1987 https://doi.org/10.1115/1.3261303
  3. Song, S. H. and Kim, J. B., 'Stress Effects on Activity of Primary Cracks Initiating at Stress Concentrator,' Journal of the KSPE, Vol. 16, No.3, pp. 145-153, 1999
  4. Brooksank, D. and Andrews, K. W., 'Stress Fields Around Inclusions and Their Relation to Properties,' Journal Iron & Steel Inst., Vol. 117, No.2, pp. 246-255, 1972
  5. Trantina, G. G. and Barishpoisky, M., 'Elastic-Plastic Analysis of Small Defect-Void and Inclusion,' Eng. Fract. Mech., Vol. 20, No.1, pp. 1-10, 1984
  6. Kitagawa, H. and Suh, C. M., 'Crack Growth Behavior of Fatigue Microcracks in Low Carbon Steels,' Fatigue Fract. Eng. Mat. Struct., Vol. 9, No. 6,pp.409-424,1987 https://doi.org/10.1111/j.1460-2695.1987.tb00468.x
  7. Kim, Y. J. and Cho, D. S., 'Mode Decomposition of Three-Dimensional Mixed-Mode Cracks using the Solution for Penny-Shaped Crack,' International Journal of the KSPE, Vol. 2, No.3, pp. 11-18,2001
  8. Mauge, C. and Kachanov, M., 'Anisotropic Material with Interacting Arbitrarily Oriented Cracks. Stress Intensity Factors and Crack-Microcrack Interactions,' InLI. Fract., Vol. 65, pp. 115-139, 1994
  9. Song, S. H. and Bae, J. S., 'Fatigue Crack Initiation and Propagation from Hole Defects,' Society for Experimental Mechanics, Vol. 38, No.3, pp. 161-166. 1998 https://doi.org/10.1007/BF02325738
  10. Song, S. H. and Lee, K. R., 'Analysis of Short and Long Crack Behavior and Single Overload Effect by Crack Opening Stress,' KSME International Journal, Vol. 13, No. 12, pp. 865- 878,1999 https://doi.org/10.1007/BF03184754
  11. Song, S. H., Lee, K. R. and Kim, A. K., 'Analysis on Short Crack Growth Rate after Single Overload under Cyclic Bending Moment,' International Journal of the KSPE, Vol. 2, No.3, pp. 19-26,2001
  12. Smith, R. A. and Lin, X. B., 'Shape Evolution of Surface Cracks in Fatigued Round Bars with a Semicircular Circumferential Notch,' Int. J. Fatigue, Vol. 21, pp. 965-973,1999 https://doi.org/10.1016/S0142-1123(99)00075-4
  13. Fonte, M. and Freitas, M., 'Stress Intensity Factors for Semi-elliptical Surface Cracks in Round Bars under Bending and Torsion,' Int. J. Fatigue, Vol. 21, No.5, pp. 457-463, 1999 https://doi.org/10.1016/S0142-1123(98)00090-5
  14. Song, S. H. and Choi, B. H., 'A Study on the Characteristics and the Prediction of the Fatigue Strength of the Induction Surface Hardened Steel,' Journal of the KSPE, Vol. 18, No.9, pp. 122-130, 2001
  15. Schijve, J. and Partl, O., 'Multiple-site Damage in 2024-T3 Alloy Sheet,' Int. J. Fatigue, Vol. 15, No.4, pp. 293-299, 1993 https://doi.org/10.1016/0142-1123(93)90378-4
  16. Murakami, Y. and Tsuru, H., 'Stress-Intensity Factor Equations for Semi-elliptical Surface Crack in a Shaft under Bending,' Stress Intensity Factors Handbook, Vol. II, pp. 653-705, 1987
  17. Nishitani, H., Takenori, M., 'Evaluation of the Characteristic of Crack Propagation of Specimen with Small Notch for Bending Loading,' Transaction of the JSME, Vol. 42, No. 354, pp. 325-334, 1976 https://doi.org/10.1299/kikai1938.42.325
  18. Carpinteri, A. and Brighenti, R., 'Fatigue Growth Simulation of Part-through Flaws in Thick-walled Pipes under Rotary Bending,' Int. I. Fatigue, Vol. 22, pp. 1-9,2000 https://doi.org/10.1016/S0142-1123(99)00115-2