초록
High temperature deformation behavior of activated sintered W powder compacts was investigated. The compression tests were carried out in the temperature range between 900 and 110$0^{\circ}C$ at the strain rate of $10^{-3}s^{-1}$. The sintered specimens of Ni-doped submicron W powder compacts showed decrease in W grain size with increasing the Ni content. As the result, the flow stress was significantly increased with increasing the Ni content. We obtained Ni-activated sintered W compacts with the relative density of 94 $\pm$ l％and the average grain size of less than 5${\mu}{\textrm}{m}$. A moderate true strain up to 0.60 was obtained without fracture even at 110$0^{\circ}C$ with the strain rate of $10^{-3}s^{-1}$ for the activated W compact despite adding the 1.0 wt％Ni to submicron W powder.