Synthesis of Alumina Nano Particles by PAA Gel Method from Kaolin

카올린으로부터 PAA Gel법에 의한 알루미나 나노 입자의 합성

  • Published : 2004.03.01

Abstract

Non-aggregated nanoscale $\alpha$-Al$_2$O$_3$ powders were prepared successfully by polyacrylamine (PAA) gel method. The method was very simple and polymer network inhibited the aggregate of $\alpha$-Al$_2$O$_3$ powders. In this investigation, nanoparticles of $\alpha$-Al$_2$O$_3$ with a diameter of about 8-15 nm were fabricated by calcining the gel precusors with various concentrations of aluminum sulfate, acrylamide and N,N'-methylene-bis-acrylamide (BIS) in air at 110$0^{\circ}C$ for 2 h. The molar ratio of aluminum sulfate to acrylamide did not have any influence on the size of particles. On the other hand, as the molar ratio of BIS to acrylamide increased, the size of nanoparticles decreased.

Polyacrylamide(PAA) 겔법은 매우 간단한 중합법이며, 고분자 망상구조가 $\alpha$-Al$_2$O$_3$ 분말의 응집을 억제하므로 미 응집된 나노 크기의 $\alpha$-Al$_2$O$_3$ 분말은 polyacrylamide(PAA) 겔법을 통하여 성공적으로 합성되었다 본 연구에서는 황산알루미늄, acrylamide 및 N,N'-methylene-bis-acrylamide(BIS)의 여러 농도에서 합성된 겔 전구체를 공기 중에서 110$0^{\circ}C$, 2시간동안 하소시켜서 약 8-l5 nm의 직경을 가진 나노 $\alpha$-Al$_2$O$_3$ 입자들을 제조할 수 있었다. Acrylamide에 대한 황산알루미늄의 몰비를 증가시켰을 때는 나노 입자들의 크기는 변하지 않았지만, acrylamide에 대한 BIS의 몰비를 증가시켰을 때는 나노입자들의 크기는 작아지는 경향을 나타내었다.

Keywords

References

  1. Nanostruct. Mater. v.10 no.6 Preparation and Properties of Intragranular Al₂O₃-SiC Nanocomposites H.Z.Wang;L.Gao;L.H.Gui;J.K.Guo https://doi.org/10.1016/S0965-9773(98)00132-9
  2. Macroporous & Mesoporous Mater. v.54 Nanostructured Ceramic Powder by hydrothermal Synthesis and their Applications C.Kaya;J.Y.He;X.Gu;E.G.Butler https://doi.org/10.1016/S1387-1811(02)00334-7
  3. J. Mater. Proc. Tech. v.93-93 Processing and Properties of Nanophase Ceramics R.Vaen;D.Stover
  4. J. Alloy. & Comp. v.341 Synthesis and Optical Properties of $Nd^{3+}$-Doped $Y_3Al_5O_{12}$ Nanoceramics D.Hreniak;W.Strek https://doi.org/10.1016/S0925-8388(02)00067-1
  5. J. Kor. Chem. Soc. v.35 no.3 A Study on the synthesis of High-Purithy α-Al₂O₃ Ultra-Fine Powders by Wet Chemical Method J.H.Choi;J.S.Yoo;Y.S.Han;J.Kim;H.K.Lee;H.N.Kim
  6. Mater. Res. Bull. v.24 no.9 The Polyacrylamide Gel : A Novel Route to Ceramic and Glassy Oxide Powders A.Douy;P.Odier https://doi.org/10.1016/0025-5408(89)90069-X
  7. Mater. Chem. & Phys. v.64 The Crystal Structure and Spectra of Nano-Scale YAG : $Ge^{3+}$ Q.Li;L.Gao;D.Yan https://doi.org/10.1016/S0254-0584(99)00250-3
  8. Mater. Sci. & Eng. v.A359 α-Fe-Al₂O₃ Nanocomposite Prepared by Sol-Gel Method Y.L.Huang;D.S.Xue;P.H.Zhou;Y.Ma;F.S.Li
  9. J. of Kor. Inst. Metal. v.28 no.3 Preparation of High Purity-Ultra Fine Al₂O₃ by Sol-Gel Method C.K.Jo;C.W.Won;B.S.Chun
  10. Mater. Res. Bull. v.36 Synthesis of Nickel Ferrite Nanoparticles by Sol-Gel Method D.H.Chen;X.R.He https://doi.org/10.1016/S0025-5408(01)00620-1
  11. Mater. Sci. & Eng. v.A288 Preparation of α-Alumina Coated Carbide Tools by The Sol-Gel Process Y.C.Chen;X.Ai;C.Z.Huang;B.Y.Wang
  12. Nanostruct. Mater. v.10 no.4 A New Sol-Gel Route Using Inorganic Salt for Synthesizing Al₂O₃ Nanopowders W.M.Zeng;L.Gao;J.K.Guo https://doi.org/10.1016/S0965-9773(98)00095-6
  13. J. Am. Ceram. Soc. v.83 no.6 Synthesis of Hydrated Aluminum Sulfate from Kaolin by Microwave Extraction S.S.Park;E.H.Hwang;B.C.Kim;H.C.Park https://doi.org/10.1111/j.1151-2916.2000.tb01390.x