Abstract
The annealing-temperature dependence of magnetic properties in compressed powder cores being composed of ball-milled F $e_{73.5}$C $u_1$N $b_3$S $i_{15.5}$ $B_{7}$ alloy powders (size 250∼850${\mu}{\textrm}{m}$) and 5 wt% of ceramic insulators has been investigated. When annealed at 5$50^{\circ}C$ for 1 h and so transformed to $\alpha$-Fe phase nanocrystalline structure with the grain size of 11 nm (electrical resistivity : 110 $\mu$Ω$.$cm), the highest effective permeability of 125 and quality factor of 53 were obtained, and the permeability persisted up to about 500 KHz. Further the core loss measured at the frequency of 50 KHz and the induction amplitude of 0.1 T was very low (230 mW/㎤). However the dc bias characteristics was not satisfactory as compared to that of conventional powder core materials(MPP, Sendust etc.). The inferior dc bias property of F $e_{73.5}$C $u_1$N $b_3$S $i_{15.5}$ $B_{7}$ alloy powder cores was attributed to the fact that the size of powder was too large for obtaining the same permeability with that of conventional materials.
F $e_{73.5}$C $u_1$N $b_3$S $i_{15.5}$ $B_{7}$ 비정질 리본 합금을 490∼61$0^{\circ}C$의 온도 범위에서 열처리하고 이를 볼 밀링 하여 얻은 250∼850$\mu\textrm{m}$크기의 자성분말과 5wt%의 세라믹 절연체로 구성된 분말 코아의 자기적 특성에 열처리 온도가 미치는 영향을 조사하였다. 5$50^{\circ}C$에서 1 h동안 열처리하여 직경 11 nm의 $\alpha$-Fe상 나노 결정립 구조로 되었을 때(전기비저항은 110$\mu$Ω$.$cm)가장 높은 실효투자율 및 품질계수를 나타내었으며 그 값은 각각 125와 53이었고, 실효투자율의 경우 약 500 KHz에 이르기까지 일정한 크기를 유지하였다. 그리고 이 열처리 조건에서 230 mW/㎤(f=50 KHz, $B_{m}$ =0.1 T)의 대단히 낮은 자심손실을 나타내었다. 그러나 이 합금의 분말 코아는 종래의 분말 코아 재료(MPP,센더스트 등)에 비해 그리 우수하지 못한 직류 바이어스 특성 특히 저 자장 하에서의 낮은 퍼센트 투자율을 나타내었는데, 이는 종래의 소재와 유사한 투자율을 얻는데 너무 큰 입도의 분말이 필요한 것에 그 원인이 있는 것으로 이해되었다.