The Combustion Safety of Waste CCA Treated Wood

폐 CCA처리재의 소각처리

This study was carried out to find out safety disposal methods of waste CCA treated wood. The heavy metals of remnant were analyzed after combustion of CCA treated wood at different temperatures. Arsenic volatilized temperature was detected. The removal rate of heavy metals by acid in the ash were examined. Through this study, we could conclude that in order to protect volatilize arsenic, combustion of CCA treated wood should be do under the $300^{\circ}C$. But when CCA treated wood combustion under $300^{\circ}C$, it's weight-loss rate was $55\%$, so land reclamation dependence will be increased. When CCA treated wood combustion at high temperature, the land reclamation dependence could be reduced, but the arsenic that volatilize into the atmosphere should be captured. When it bums with high temperature, the ash contains lots of copper and chromium, so removal of heavy metals should be conducted.

사용이 끝난 폐 CCA 처리재의 폐기를 위한 안전한 소각 방법을 찾고자 본 시험을 실시하였다. CCA 처리재를 온도를 달리하여 소각한 후 중금속의 잔존량을 측정하였으며, 동시에 비소가 비산되는 온도조건을 탐색하였다. 그리고 소각처리가 끝난 소각재 내에 잔존하는 CCA 유효성분인 중금속을 다양한 용제로 회수한 후 회수율을 비교하였다. 연소 후, 잔존하는 중금속 분석에서 비소는 $300^{\circ}C$에서는 비산되지 않음을 알 수 있었다. CCA 처리재를 저온으로 연소하면 비소의 비산은 방지 할 수 있으나, $300^{\circ}C$에서 중량감소율이 $55\%$에 머물러 소각 후 잔류물을 매립하여야 하는 문제점이 있다. 따라서 고온으로 소각 시 비산되는 비소를 포집할 수 있는 효과적인 방법 마련이 필요하며, 고온으로 소각하여도 소각재중에는 크롬과 구리가 다량으로 함유되어 있으므로 적절한 방법으로 이들을 회수하는 방법이 마련되어야 한다. 실험결과 소각재중에 남아있는 중금속 회수에는 $10\%$ 질산으로 처리한 것이 가장 효과적이었다.