(Dept. of Clothing and Textiles, Ewha Womans University)
;
(Dept. of Clothing and Textiles, Ewha Womans University)
A new textile material, poly(trimethylene terephthalate) polymer, has been introduced to the textile industry. The structure of PTT is similar to the PET, while the tensile deformation and subsequent recovery property is better than that of PET. In this study, the physical and mechanical properties of textile woven fabrics made of PTT, PET, and nylon 6 yarns as the filling yarn were determined using the Kawabata Evaluation System (KES), including tensile, bending, shearing, compression, and surface related parameters. On top of these measurements, the subjective ratings by evaluators were performed on the fabric samples. From the examination of the stress-strain behavior of the yarn specimens focused on the recovery mode, it was evident that the PTT specimen developed lower stress at 3% elongation. The subsequent recovery curve showed that the PTT has less stress-decay rate than the other specimens, implying that the recovery behavior of the PTT is recommendable for the end-uses including stretchable textile materials, sports wears, etc. The KES bending rigidity(B) value of the PTT sample fabric was lower than that of the PET sample fabric. Subjective evaluation of the fabric samples by the evaluators on the descriptive word pair "soft - not soft" showed similar tendency with the KES B determination of the fabric samples.