Abstract
The micro structure of POY was modified and a wool-like touch yarn of composite fibers with different shrinkage was made. With this yarn 12 different fabrics with wool like touch were prepared. The characteristic physical property changes of the fabrics examined are as follows: 1. In all cases, the initial high shrinkage stages were observed in hot water treatment and the 3D images of complex multilayer of typical doubling fibers with different shrinkage were also observed in hot air treatment of 170C. 2. The tensile strength changes of satin and plain fabrics with the change of twist count showed similar behavior. However, WT's were slightly higher and RT's was lower in twill and satin fabrics than those in plain fabric. 3. Since a slight decrease of B's of twill fabric found with increasing twist count under given experimental condition, it could be influenced on the anti-drape stiffness was decreased and flexibility was increased. 4. A significant decrease of G values was observed in the twist count 800-1000 T.P.M However, in the twist count higher than 1000 T.P.M G values observed were kept nearly constant. 5. MIU of plain and twill fabrics showed a drastic decrease at the twist count higher than 1000 T.P.M.