DATA and FT-IR absorption spectra of PbO-Bi₂O₃-B₂O₃-SiO₂ glasses

PbO-Bi₂O₃-B₂O₃-SiO₂ 유리계 열시차분석과 FT-IR 흡수 스펙트럼

The experimental FT-IR spectra and DTA curves of the $PbO-Bi_2O_3-B_2O_3-SiO_2$ glasses have been investigated. The composition ratio dependence of glass transition temperature showed that the structure of this glass system changes at 60 mol% $Bi_2O_3$. We have observed that the FT-IR spectra of the investigated samples with high bismuth content are dominated by bands associated to the structural units of the heaviest cation, $Bi^{3+}$ and the boron atoms in the treated samples are three and four coordinated even for very high $Bi_2O_3$ content. The low intensity of these non-bridging oxygen bands, for high PbO content glasses, can be attributed to the strong network-forming roles of PbO. The glasses absorption bands exhibited a greater change in intensities on crystallization.

$PbO-Bi_2O_3-B_2O_3-SiO_2$ 유리계의 DTA 곡선과 FT-IR 스펙트럼을 조사하였다. 유리전이 온도의 조성비 의존성은 60 mol% $Bi_2O_3$에서 유리계의 구조가 변화하는 것으로 나타났다. 높은 비스무스 함량을 가지는 시료의 FT-IR 스펙트럼 조사에서 무거운 양이온 $Bi^{3+}$의 단위구조와 관계되는 결합이 우세했으며 그리고 고함량의 $Bi_2O_3$ 시료에서도 역시 붕소원자의 3배위와 4배위 진동이 있었다. PbO함량이 높은 유리계의 경우, 비가교 산소밴드의 낮은 강도는 PbO의 망목형성제 역할에 기인 한 것으로 생각된다. 유리의 흡수대는 결정화상태에서 강도가 매우 큰 변화를 보였다.