The Effects of Crosslinking Agent and pH Controlling Agent on Adhesive Properties of Water Soluble Acrylic PSA

가교제 및 pH 조절제가 수용성 아크릴 점착제의 점착 물성에 미치는 효과

In this paper, the effects of crosslinking agent and pH controlling agent on adhesive properties and water solubility of water soluble acrylic pressure sensitive adhesives were studied by adding the crosslinking agents or pH controlling agents after the polymerization. the tack, cohesive strength, and peel strength were measured to evaluate adhesive properties. the turbidity was also measured to evaluate water solubility of pressure sensitive adhesives. When crosslinking agent was added less than 0.2 wt%, tack increased and cohesive strength and peel strength decreased with increasing concentration. When crossinking agent was added more than 0.2 wt%, the results were opposited. When pH controlling agent was added, tack and water solubility decreased and peel strength and cohesive strength increased with increasing concentration. the influence of pH controlling agents on adhesive properties and water solubility of pressure sensitive adhesive increased in the order of lithium hydroxide, potassium hydroxide and sodium hydroxide.

본 연구에서는 점착제의 유지력 개선과 pH 조절을 위해 각각 첨가해 주는 가교제와 pH 조절제의 종류 및 첨가량이 수용성 아크릴 점착제의 점착 물성 및 수용성에 미치는 효과를 알아보기 위하여 중합된 점착 시료에 여러 가지의 가교제와 pH 조절를 첨가해 준 후 초기점착력, 유지력 및 점착력 등의 점착 물성과 수용성을 측정하였다. 가교제를 0.2 wt% 미만 첨가해 주었을 때, 초기 점착력은 감소하였고 유지력과 점착력은 증가하였다. 그러나 0.2 wt% 이상 첨가해 주었을 때는 초기 점착력은 증가하였지만 유지력과 점착력은 감소하는 결과를 보였다. 또한 pH 조절제를 첨가해 주었을 때 pH 조절제의 농도가 증가함에 따라 초기점착력과 수용성은 감소하였고 점착력과 유지력은 증가하였으며, LiOH, KOH, NaOH 순으로 점착 물성과 수용성에 미치는 영향이 큰 것으로 나타났다.