Abstract
This experiment was carried out to examine the effect of iron oxide roasting for Sr-ferrite magnet. Chloride content was decreased with raising the 2 nd roasting temperature of iron oxide for ruthner process iron oxide. The optimization temperature for roasting of ruthner process iron oxide was around $800^{\circ}C$ as average particle size 1.5∼1.9 $\mu\textrm{m}$, apparent bulk density 1.4 g/$m\ell$ and chloride content 0.05%. The relation between Br and HcJ by sintering temperature for Sr-ferrite magnet was found to be Br≒-0.258HcJ＋494. In case of having a vibrating disk mill for the ruthner process iron oxide, the magnetic properties were Br 421 mT and HcJ 251 kA/m.
제철소 냉연 공정의 염산 폐액에서 ruthner process 공법으로 제조된 산화철을 사용하여 2차 배소 온도변화에 따른 산화철의 분체 특성을 조사하였고, 산화철과 스트론튬을 건식 혼합 및 가소후 Sr-ferrite 자석을 제조하여 자기적 물리적 특성을 조사하였다. Ruthner proces의 산화철을 2차 배소를 실시한 경우, Cl- 함량이 적고 분체 특성이 안정적인 배소온도는 $800^{\circ}C$ 부근으로, 평균 입자(APS)는 1.5 $mu extrm{m}$, apparent bulk density(ABD)는 1.4 g/$m\ell$ 이며, Cl- 함유량은 0.05% 이하를 나타내었다. Ruthner process에서 제조된 산화철을 vibrating disk mill에서 1차 분쇄를 실시한 경우, Sr-ferrite magnet의 보자력(HcJ)은 229 kA/m에서 251 kA/m로 향상하였다. Sr-ferrite magnet의 소결 온도 변화에 따른 잔류자속밀도와 보자력의 희귀식은 Br≒-0.258HcJ＋494의 함수 관계를 나타내고 있으며, 성형 중 가한 자장 방향과 수직방향에 따른 수축비는 산화철의 2차 배소 온도 $800^{\circ}C$까지는 1.6으로 안정적인 판상형으로 결정 성장을 나타내고 있으나, 그 이상의 온도로 2차 배소한 산화철을 사용한 경우에는 소결에서 결정이 더 커진 것으로 판단된다.