Abstract
According to the recent trend to raise the horizontal scan frequency to increase the image refinement of the High Definition TV and High Resolution Display, material with low core loss is required for the ferrite core for deflection yoke, which is secured even in the high frequency range. liking notice of the influence on the fine structure of Mg-Zn ferrite by the chemical com position and process, low temperature sintering was proceeded. Cu was added to the low loss Mg-Zn system ferrite. After select-ing MgO, ZnO, $Fe_2$$O_3$, CuO, MgO was substituted for CuO while varying the composition ratio. Then the sample was sintered for 3 hours between $980～1350^{\circ}C$ Magnetic permeability, power consumption, shrinkage rate, core loss were measured. The start-ing temperature to test the shrinkage of the sample was nearby $900^{\circ}C$, it increased according to the substitution process of Cu, and the firing temperature was lowered about $-50～-75^{\circ}C$ alongside of the process.
본 논문에서는 최근 고품위 TV 및 고정세도 디스플레이용으로 화상의 정세도를 향상시키기 위해 수평주파수를 높이려는 움직임이 있어, 편향 요크용 페라이트 코아에는 고주파수 영역에 있어서도 코아로스가 낮은 재료가 요구되고 있는 실정이다. Mg-Zn 페라이트에 있어서 화학조성 및 프로세스가 미세구조에 미치는 영향에 착안하여 저온 소결화를 하였다. 저손실인 Mg-Zn계 Ferrite에 Cu를 첨가하였다. MgO, ZnO, $Fe_2$$O_3$, CuO를 선택한 후 조성비의 변화를 두며 CuO를 MgO로 치환하였다. 이 시료를 $980∼1350^{\circ}C$까지 3시간 소결하였다. 측정은 투자율, 전력손실, 수축율, 코아로스를 측정하였다. 시료의 수축율을 개시하는 온도는 $900^{\circ}C$부근이며 Cu치환에 따라 수축율이 증가하였으며, Cu 치환에 따라 소성온도가 약 $-50∼-75^{\circ}C$ 낮아졌다.