As concrete structures are getting larger, higher, longer, and specialized, it is more required to develop steel fiber concrete and apply to the real world. In this research, it is aimed to have fatigue strength examined, varying the steel fiber content by 0%, 0.75%, 1.00%, 1.25%, by experimental study of Two-spans Beam with Steel Fibrous with repeated loads. The ultimate load and the initial load of flexural cracking were measured by static test. In addition, the load versus strain relation, load versus strain relation, load versus deflection relation, crack pattern and fracture mode by increasing weight was observed. On the other hand, the crack propagation and the modes of fracture according to cycle number and the relation of cycle loading to deflection relation and strain relation was observed by fatigue test. As the result of fatigue test, Two-spans Beam without Steel Fibrous was failed at 60~70% of the static ultimate strength and it could be concluded that fatigue strength to two million cycle was around 67.2% by S-N curve. On the other hand, that with Steel Fibrous was failed at 65~85% of the static ultimate strength and it could be concluded fatigue strength to two million cycle around 71.7%.
최근 콘크리트 구조물이 점차 대형화, 고층화, 장대화 및 특수화 됨에 따라 강섬유 콘크리트의 적용이 요구되고 있다. 본 연구에서는 반복하중을 받는 강섬유를 혼입한 2경간 연속보에 대한 실험적 연구를 수행하여 피로하중에 의한 강섬유 혼입율(0%, 0.75%, 1.00%, 1.25%)에 따른 피로강도를 규명하고자 하였다. 정적실험을 통하여 극한하중, 초기 휨균열하중 등을 측정하였고 하중과 철근의 변형율 관계, 하중과 처짐 관계 그리고 하중증가에 따른 균열성장과 파괴양상 등을 관찰하였다. 피로실험을 통하여 반복횟수와 처짐 관계, 반복횟수와 변형율 관계 그리고 반복횟수에 따른 균열성장과 파괴양상을 관찰하였다. 피로실험 결과 강섬유를 혼입하지 않은 2경간 연속보는 정적극한강도의 60~70%에서 파괴되었고 S-N곡선으로부터 반복횟수 200만회에 대한 피로강도는 정적극한강도의 67.2% 전후임을 확인 할 수 있었다. 또한, 강섬유를 혼입한 2경간 연속보는 정적극한강도의 65∼85%에서 파괴되었고 S-N곡선으로부터 반복횟수 200만회에 대한 피로강도는 정적극한강도의 71.7%전후임을 확인할 수 있었다.