Abstract
Effects of additives and plating conditions of high speed electroplating were investigated. The Sn content in electrodeposit was highly decreased with increasing current density from $10A/dm^2$ to $50A/dm^2$, and the current efficiency on the cathode was decreased. The carbon content in the electrodeposit was decreased with increasing current density from $10A/dm^2$ to $30A/dm^2$, however the carbon content was highly increased in the range of $40A/dm^2$$∼50A/dm^2$. The formation of tetravalent tin and stannic oxide sludge was prevented by the addition of gallic acid in the bath. The changing of Sn content in the electrodeposit is caused by the addition of gallic acid.