Abstract
The crystallization behavior of a luster glaze containing ceria has been investigated. When glazed specimens were sintered at 110$0^{\circ}C$, crystalline ceria particles were preferentially precipitated with (100) planes parallel to the specimen surface with the size of around 200 nm. The particle population in the surface region was much higher than inside glaze, covering over 60% of the specimen surface area. Crystallization of the particles with preferred orientation was promoted, after the removal of internal interface through complete melting of the fit particles. The luster effect seems to result from CeO$_2$ particles of high refractive index, their strong light scattering at visible rage due to fine crystalline size 200 nm and their planar arrangement in the surface region.
장석, 규석, 석회석 등의 천연원료와 CeO$_2$를 출발원료로 하여 프릿 형태의 러스터 유약을 제조하고 결정화 특성과 러스터 효과의 발현기구를 분석하였다. 시유한 시편이 110$0^{\circ}C$에서 소성되었을 때, 유면과 수평한 방향으로 (100)면이 배향된 200nm 크기의 CeO$_2$ 결정이 시편의 표면에 생성되었다. 표면에서 결정화된 입자의 빈도는 유약의 내부보다 훨씬 높았으며, 전체 표면적의 60% 이상을 배향된 CeO$_2$ 결정이 점유하였다. 배향된 CeO$_2$ 결정립은 유약내의 프릿 입자가 완전히 용융되어 내부 계면이 사라진 이후부터 발달하기 시작하였다. 본 연구에서 개발된 유약의 러스터 효과는 유약표면에 석출된 CeO$_2$가 고굴절을 갖는 물직일 뿐만 아니라 최대 산란을 일으키는 결정크기(200nm)이고 판상형태로 배열되어 있기 때문인 것으로 판단된다.