Abstract
In this paper, the fracture strength of the surface damaged laminates was predicted by applying the fracture strengths of the unflawed and flawed laminates. For prediction, the theoretical equation about the fracture strength of laminates was simplified applying classical laminate theory and was applied to the surface damaged laminates. Lagace's and Tsai's experimental data were used for verifying the theoretical equation. Moreover, to verify the theoretical prediction, an experiment was performed. Surface unflawed laminate and flawed laminates were fabricated and the experiments were made and these results were compared with theoretical predictions. The specimens' fiber direction was same to the tensile direction and the theoretical predictions and the experimental results were showed good agreement. Therefore, by this equation, the fracture strength of structures made of composites will be able to be predicted when the surface of the structures was damaged.
본 논문에서는 표면 손상을 입은 적층판의 파괴 강도를 결함이 없는 적층판의 파괴 강도와 결함이 있는 적층판의 파괴 강도를 이용하여 예측하였다. 이를 위해 고전 적층판 이론을 적용하여 적층판의 파괴 강도식을 단순화했으며 이를 표면 손상을 입은 적층판에 적용하였다. 단순화한 적층판의 파괴 강도 이론식의 검증을 위해 Lagace와 Tsai의 논문에서 측정한 데이터를 이용하였다. 또한, 표면 손상을 입은 적층판의 파괴 강도 예측식의 검증을 위해 실험을 수행하였다. 실험을 위해 표면 결함이 없는 적층판과 표면 결함이 있는 적층판을 제작하여 실험하였으며 이 결과를 예측식과 비교하였다. 시편의 섬유 방향은 인장 방향과 같은 방향으로 제작되었으며, 예측식과 실험 결과는 잘 일치하였다. 따라서 본 논문에서 예측만 표면 결함이 있는 적층판의 파괴 강도 예측식을 이용하여 복합재료가 사용되는 구조물이 표면 손상이 되었을 때 이 구조물의 파괴 강도를 예측할 수 있을 것이다.