Abstract
The multi-layered OELDs(organic electroluminescent devices) were prepared on the patterened ITO (indium tin oxide)/glass substrates by the vacuum thermal evaporation method. The $Alq_3$ (tris-(8-hydroxyquinoline)aluminum) low molecule compound was used as the light emission layer. TPD(triphenyl-diamine) and $\alpha-NPD$ were used as the hole transport layer. CuPc (Copper phthalocyanine) was also used as the hole injection layers. In addition, QD2 (quinacridone2) organic material with $10\AA$ thickness was deposited in the $Alq_3$ emission layer to improve the luminance efficiency. The threshold voltage was about 7V for all devices. The luminance and efficiency of devices was improved by substitution the $\alpha-NPD$ for TPD as the hole as the hole transport layer. The luminance efficiency of the OELD sample with QD2 thin film in the $Alq_3$ emission layer was found to be 1.55 lm/W, which is about 8 times larger value compared to the sample without QD2 thin layer.
본 연구에서는 ITO (indium tin oxide)/glass 투명기판 위에 다층구조의 OELD (organic electroluminescent devices) 소자를 진공 열증착법으로 제작하였다. 발광층 재료로서 Alq$_3$(tris-(8-hydroxyquinoline)aluminum)물질을 사용하였고, 정공수송층으로는 TPD (triphenyl-diamine) 및 $\alpha-NPD$를 사용하였다. 정공주입층 재료로서 CuPc (Copper phthalocyanine)를 사용하였다. 또한 QD2(quinacridone2) 물질을 $Alq_3$ 발광층내에 약 $10\AA$ 두께로 증착하여 발광효율 향상을 시도하였다. 제작된 모든 소자의 발광개시전압은 약 7 V 이었으며, 정공수송층으로 TPD 물질대신에 열적안정성이 우수한 $\alpha-NPD$를 사용한 경우 휘도값과 발광효율이 개선되었다. $Alq_3$ 발광층 사이에 QD2 물질을 적층한 소자에서 발광효율은 1.55 lm/W 값을 나타내어 $Alq_3$ 발광층만을 사용한 경우에 비해 약 8배 발광효율이 향상되었다.