Preparation and Application of Microcapsule - Preparation and Properties of Suspension-Polymerized Poly(vinyl alcohol) Microsphere with Core-Shell Structure -

마이크로캡슐의 제조와 응용 - 분산중합에 의한 core/shell 구조를 지닌 Poly(vinyl alcohol) Microsphere의 제조와 특성 -

  • Published : 2003.08.01
Download PDF
⟨ Previous Next ⟩

Abstract

Poly(ethylene-co-vinylacetate) (EVA) microspheres were prepared by a thermally induced phase separation. Poly(vinyl Alcohol) (EVAL) microsphere with Core-Shell Structure were synthesized by a saponification on sheath of EVA microspheres. The size of EVA core/EVAL shell microsphere was decreased from $4.09\mu{m}\;to\;2.55\mu{m}$ by partial saponification of $NaOH/Na_2SO_4$/methanol(2 : 1 : 1 by weight) at $60^\circ{C}$ for 4h to produce a saponified surface layer of about 60% of original radius. In this process, the surface layer of EVAL microsphere was dissolved partially and morphology of surface was not showed. Add-on of cotton and silk printed with EVA core/EVAL shell microsphere was increased and that of printed PET was decreased. In case of EVA core/EVAL shell microsphere, Hand of cotton and silk printed was flexible and fullness.

Keywords

References

  1. Apparel Ind. Mag. v.56 Freeing the bottle neck J.W.Dewitt
  2. Georgia Institute of Technology M.S. thesis Toners for xerographics textile printing produced via Thermally induced phase seperatin H.S.Park
  3. Text. Chem. and Color v.23 no.5 W.W.Carr;F.L.Cook;W.R.Lanigan;M.E.Sikorski
  4. Journal of Electrostatics v.43 Studies on toners for textile xerography W.W.Carr;D.D.Sarma;F.L.Cook
  5. Georgia Institute of Technology M. S. Thesis Xerographic printing of textiles B.J.Failor
  6. J. Ploy. Sci. Plym. Chem. Ed. v.8 Molecular weight development in constant-rate styrene emulsion polymerization M.R.Grancio;D.J.Williams
  7. J. Poly. Sci. Plym. Chem. Ed. v.8 The morphology of the monomer-polymer particle in styrene emulsion polymerization M.R.Grancio;D.J.Williams
  8. J. Poly. Sci. Plym. Chem. Ed. v.11 no.1 Equilibrium encapsulation of polystyrene latex particles P.Keusch;D.J.Williams
  9. J. Poly. Sci. Plym. Chem. Ed. v.11 Particle morphology inemulsion polymerization D.J.Williams
  10. J. Poly. Sci. Plym. Chem. Ed. v.12 Latex particle morphology during polymerization and at saturation equillibrium D.J.Williams
  11. Macromolecules v.7 Polymer segment density distributions insaturated P.Keusch;R.A.Graff;D.J.Williams
  12. Nippon Kagaku Kaishi v.5 Synthesis and properties of hydrophillic gels prepared by the crosslinkage of ply(vinyl alcohol) C.Hirayama;K.Kawagachi;Y.Motoazato
  13. Journal of Applied Polymer Science v.46 Synthesis and characterization of suspension-polymerized poly(vinyl alcohol) beeds with core-shell structure C.J.Kim;P.I.Lee
  14. The Korean Fiber Society v.36 no.1 Study on the functional microsphere - Modification and Property of EVA Microsphere Using Polyurethane(1) H.S.Lee;K.P.Kim;H.I.Kim;B.H.Ahn;S.M.Park
  15. JAPS v.47 Graft copolymers from modified EVA copolymer R.V.Barbosa;B.G.Soares;A.S.Gomes
  16. European Polymer Journal v.38 no.4 Graft copolymers from modified EVA copolymer F.G.Garcia;M.R.Pinto;B.G.Soares
  17. Macromolecules v.29 Graft copolymers from modified EVA copolymer(3) M.A.R.Moraes;A.C.F.Moreira;R.V.Barbosa;B.G.Soares
  18. Polymer Bulletin v.36 Poly(ethylene-co-vinyl alcohol-co-vinyl mercap-toacetate) (EVALSH)-determination of vinyl mercaptoacetate content by thermogravimetric analysis and FTIR spectroscopy R.C.L.Dutra;V.L.Lourenco;M.F.Diniz;M.F.P.Azevedo;R.V.Barbosa;B.G.Soares