Study on Plastic Fiber Coating Materials

플라스틱 직물 코팅재료에 관한 연구

Liquid PVC, which is used widely as fiber coating, has brilliant non-luster effect, but it decreases flexibility of coated fiber surface. We used liquid silicone rubber in elastomer series as a coating material to alleviate this problem. We have conducted the former liquid PVC processing and used pressure of roller and preliminary hardening of processing. In this experiment, We measured 70 degree of hardness, 10.3 MPa of tensile strength and 200fs of tensile elongation of Liquid PVC-coated plastic fiber. We measured 40 degree of hardness, 5.1 MPa of tensile strength and 460% of tensile elongation of Liquid silicone PVC-coated plastic fiber. Therefore, Without the second process, Liquid silicone rubber coating increased non-luster effect and flexibility of plastic fiber surface more than Liquid PVC coating.

섬유 코팅제로 널리 쓰이고 있는 액상 PVC는 여러 가지 특성 중 무광택 효과가 뛰어나지만 코팅된 섬유 표면의 유연성이 감소된다. 이런 결함을 대체할 수 코팅 물질로 Elastomer계열의 액상 실리콘 고무를 사용했다. 기존 액상 PVC공정과 동일하게 진행했으며, 로울러의 압축력과 공정상의 예비경화를 이용했다. 실험 결과 액상 PVC로 코팅된 직물의 경도는 70E, 인장강도는 10.3 MPa, 신율은 200%로 측정되었다. 액상 실리콘 고무로 코팅된 직물의 경도는 40도, 인장강도는 5.1 MPa, 신율은 460%,였다. 따라서 액상 실리콘 고무 코팅은 3차 가공 없이 액상 PVC 코팅보다 플라스틱 직물 표면의 무광택성과 유연성을 증가시켰다.