Properties of Sr-Ferrites Prepared by Spark Plasma Sintering Process

스파크 플라즈마 소결법으로 제조된 Sr-페라이트의 특성

  • 노재승 (금오공과대학교 신소재시스템공학부) ;
  • 오명훈 (금오공과대학교 신소재시스템공학부)
  • Published : 2003.02.01
Download PDF
⟨ Previous Next ⟩

Abstract

Anisotropic Sr-ferrites were prepared by the spark plasma sintering process (SPS). The Ferrite particles were oriented and densified during sintering process, and the anisotropic ferrites were manufactured at low sintering temperature and a remarkable short time processing by SPS method. It was showed that the anisotropy of ferrite particles at the specimen outer side was more higher than that at the specimen center, and it seems possible that the orientation of ferrite particles was related to DC current. Magnetic and physical properties of sintered Sr-ferrites are Br = 3.15 kG, iHc : 2.67 kOe, and density : 5.033 g/cm$^3$ when the samples were sintered for 8 minutes at 106$0^{\circ}C$.

스파크 플라즈마 소결(SPS)을 이용하여 이방성 Sr페라이트 자석을 제조하였다. SPS 장치를 이용하여 소결과 동시에 페라이트 분말을 배향시킬 수 있었으며, 낮은 온도 및 짧은 작업시간으로 치밀한 이방성 페라이트 자석을 제조할 수 있었다. 페라이트 입자의 이방성은 소결체의 바깥쪽부분에서 더 크게 나타났으며, 페라이트 입자의 배향은 SPS 전류와 밀접한 관계가 있는 것으로 판단되었다. 106$0^{\circ}C$에서 8분간 소결시킨 소결체의 밀도는 5.033 g/$cm^3$이었고, 소결체의 radial plan게서 잔류 자속 밀도는 3.15 kG, 보자력은 2.67 kOe이 얻어졌다.

Keywords

References

  1. J. of the Soc. Powder Tech. Jap. v.30 Tokida M. https://doi.org/10.4164/sptj.30.11_790
  2. J. Mat. Sci. v.34 T. Takeuchi;E. Betourne;M. Tabuchi etc. https://doi.org/10.1023/A:1004506905278
  3. High Temp v.37 N. Zavodov;A. V. Kozlov;S. N. Luzganov;V. P. polishchuk;A. V. Shurhpov
  4. J. Euro. Cer. Soc. v.20 J. F. Li;S. Satomi;R. Watanabe;N. Omori;T. Hitai https://doi.org/10.1016/S0955-2219(00)00045-5
  5. Mat. Sci and Eng. v.A287 M. Omori
  6. J. Kor. Met. Ins. v.7 Y. I. Jang;J. S. Kim;I. S. Ahn;Y. D. Kim;Y.S. Kweon
  7. J. Kor. Assoc. Cry. Growth v.11 S. J. Kiml;K. S. Cho;;N. J. Park
  8. J. Kor. Met. Ins. v.8 S. J. Lee;W. J. Lee
  9. J. Kor. Cer. Soc. v.38 K. S. Cho;S. J. Kim;S. H. Beak;H. J. Choi;J. G. Lee
  10. J. Kor. Cer. Soc. v.38 K. H. Kom;K. B. Shim
  11. J. Kot. Met. Ins. v.9 Y. S. Kwon;S. G. Kim;H. S. Kim;H. T. Kim;S. I. Choi;M. J. Suk
  12. J. Mat. Res. v.14 Z. G. Liu;M. Umemoto;S. Hirosawa;H. Kanekiyo https://doi.org/10.1557/JMR.1999.0340
  13. Mat. Res. Bull. v.35 K. Hiroto;Y. Takano;M. Yoshinaka;O. Yamaguchi https://doi.org/10.1016/S0025-5408(00)00308-1
  14. J. Magnetism and Magnetic Mat. v.235 S. Yamamoto;S. Horie;N. Tanamachi;H. Kurisu;M. Matsuura https://doi.org/10.1016/S0304-8853(01)00341-9
  15. J. Magnetism and Magnetic Mat. v.239 G. Obara;H. Yamamoto;M. Tani;M. Tokita https://doi.org/10.1016/S0304-8853(01)00649-7
  16. Ceramic Bull. v.41 P. A. Denes
  17. J. Am. Ceramic Society v.70 P. Reynen https://doi.org/10.1111/j.1151-2916.1987.tb04847.x
  18. J. Kor. Cer. Soc. v.26 D. S. Kim;D. Y. Kim;W. Y. Jeung;J. H. Oh
  19. J. Kor. Inst. Eletrical and Electronic Mat. Eng. v.5 B. D. Chumg;H. W. Moon;K. S. Seo;Y. J. Shin
  20. Ceramist v.2 W. Y.Jeung
  21. J. Magnetism and Magnetic Mat. v.203 N. Murillo;J. Gonzalez;C. Guraya;M. Gutierrez;F. J. Seco https://doi.org/10.1016/S0304-8853(99)00251-6
  22. J. Kor. Magnetics Soc. v.4 W. Y. Jeung;T. S. Cho;T.J. Moon