Decomposition of Carbon Dioxide Using Sr Ferrites with Various Compositions

다양한 조성의 Sr 페라이트를 이용한 CO2분해 반응 특성

  • 신현창 (아주대학교 재료공학과) ;
  • 최정철 (아주대학교 재료공학과) ;
  • 정광덕 (한국과학기술연구원 나노-환경 연구센터) ;
  • 최승철 (한국과학기술연구원 나노-환경 연구센터)
  • Published : 2003.02.01
Download PDF
⟨ Previous Next ⟩

Abstract

Sr ferrites with various compositions were applied to the decomposition of $CO_2$ to mitigate the greenhouse effect. In the reduction reaction of Sr ferrites up to 80$0^{\circ}C$, starting temperature was lower with increasing of Sr content in Sr ferrite. However, the reactivity was higher with decreasing Sr content. In the $CO_2$ decomposition reaction with reduced Sr ferrites, the amount of CO and C were depended on the ratio of Sr and Fe in Sr ferrite. With increasing Sr content. larger amount of C were deposited on the surface of ferrite. Therefore, in order to apply Sr ferrites for the decomposition of $CO_2$, it is necessary to control the ratio of Sr and Fe according to the conditions used.

지구온난화의 주요원인인 $CO_2$의 분해를 위해 다양한 조성의 Sr 페라이트를 이용하여 $CO_2$분해능을 비교하였다. Sr 페라이트를 80$0^{\circ}C$까지 환원시킨 결과, Sr 페라이트 내 Sr 함량이 감소할수록 높은 온도에서 환원반응이 시작되었지만, 온도가 증가함에 따라 그 환원반응성은 높아졌다. 환원된 Sr 페라이트를 이용한 $CO_2$분해 반응에서는 Sr:Fe 조성비에 따라CO나 C의 생성량이 달라졌다. 이 반응에서 Sr 페라이트 내 Sr의 비율이 감소할수록 CO의 생성량은 증가하였으며, Sr의 비율이 증가할수록 페라이트 표면에 많은 양의 C가 흡착되었다. 따라서, $CO_2$분해 반응에 Sr 페라이트를 적용할 경우, 사용 조건에 따라 Sr:Fe의 조성비를 제어할 필요가 있다.

Keywords

References

  1. Int. J. Energy Res. v.23 The Fate of $CO_2$ Hydrate Released in the Ocean H. Teng;A. Yamasaki;Y. Shindo https://doi.org/10.1002/(SICI)1099-114X(19990325)23:4<295::AID-ER478>3.0.CO;2-D
  2. Applied Catalysis A; General v.165 no.2 Promotion Effect of Pt, Pd and Rh Noble Metals to the $Ni_{0.03}Mg_{0.97}O$ Solid Solution Catalysts for the Reforming of $CH_4\;with\;CO_2$ Y. Chen;K. Tomishige;K. Yokoyama;K. Fujimoto https://doi.org/10.1016/S0926-860X(97)00216-0
  3. Applied Catalysis A; General v.177 no.2 A Gel-oxalate Co-precipitation Process for Preparation of $Cu/ZnO/Al_2O_3$Ultrafine Catalyst for Methanol Synthesis from $CO_2+H_2$:(II)Effect of Various Calcination Conditions Y. Ma;Q. Sun;D. Wu;W. Fan;J. Deng https://doi.org/10.1016/S0926-860X(98)00266-X
  4. J. Catalysis v.157 no.2 Mechanisms of Methanol Synthesis from Carbon Dioxide and from Carbon monoxide at Atmospheric Pressure over Cu/ZnO S. Fujita;M. Usui;H. Ito;N. Takezawa https://doi.org/10.1006/jcat.1995.1306
  5. Nature v.346 Complete Reduction of Carbon Dioxide to Carbon Using Cation-0excess Magnetite Y. Tamaura;M. Tabata https://doi.org/10.1038/346255a0
  6. J. Kor. Ceram. Soc. v.37 no.1 Decomposition of $H_2O$with ferrite Powders for Hydrogen Generation H. C. Shin;K. D. Jung;S. H. Han;S. C. Choi
  7. J. Mater. Sci. v.29 Decomposition of Carbon Dioxide to Carbon by Hydrogen-Reduced Ni(II)-bearing Ferrite J. Kato;T. Kodama;M. Tsuji;Y. Tamaura https://doi.org/10.1007/BF00349965
  8. J. Mater. Sci. v.28 Decomposition of $CO_2$ and CO into Carbon with Active W stite Prepared from Zn(II)-bearing Ferrite T. Kodama;M. Tabata:K. Tominaga;T. Yoshida;Y. Tamaura https://doi.org/10.1007/BF00357836
  9. J. Mater. Sci. v.28 $CO_2$ Decomposition with Oxygen-deficient Mn(II) Ferrite M. Tabata;Y. Nishida;T. Kodama;K. Minori;T. Yoshida;Y. Tamaura https://doi.org/10.1007/BF00400881
  10. J. Kor. Ceram. Soc. v.39 no.8 Preperation and Charaterization of Ferrite Supported on Porous Ceramic Fiber Composites for $CO_2$Decomposition B. S. Lee;M. S. Kim;S. C. Choi;J. H. Oh;J. C. Lee https://doi.org/10.4191/KCERS.2002.39.8.801
  11. J. Mater. Sci. v.28 Carbon Dioxide Decomposition into Carbon with the Rhodium-bearing Magnetite Activated by $H_2-reduction$ K. Akanuma;K. Nishizawa;T. Kodama;M. Tabata;K. Minori;T. Yoshida;M. Tsuji;Y. Tamaura https://doi.org/10.1007/BF00400865
  12. Chem. Mater. v.13 no.4 Mechanism of M Ferrite (M=Cu and Ni) in the $CO_2$ Decomposition Reaction H. C. Shin;S. C. Choi;K. D. Jung;S. H. Han https://doi.org/10.1021/cm000658b
  13. J. Kor. Ceram. Soc. v.39 no.7 Decomposition of $CO_2$ with Recuced Ferrite by $CH_4$ H. C. Shin;K. D. Jung;O. H. Joo;S. H. Han;J. W. Kim;S. C. Choi https://doi.org/10.4191/KCERS.2002.39.7.657
  14. Energy Eng. J v.8 no.1 $CO_2$ Gas Decomposition with Sr Ferrite H. C. Shin;C. Kim;J. C. Choi;M. Tsuji;S. C. Choi
  15. IEEE Tran. Magn. v.30 no.6 Structure and Magnetic Properties of $Gd_{1-x}Sr_xFe_{3-{\delta}}$ Compounds C. S. Kim;Y. R. Um;S. I. Park;S. H. Ji https://doi.org/10.1109/20.334265