Abstract
This study has investigated the temperature-sensitive liposomes, which release anticancer drug(doxorubicin) at the hyperthermia temperature$(~40^{\circ}C)$. The temperature-sensitive liposomes were modified with a copolymers of N-isopropylacrylamide(NIPAAm) and acrylamide(AAm), which exhibit a lower critical solution temperature (LCST) at the hyperthermia temperature. The release of doxorubicin from the modified liposomes was determined by measuring the fluorescence intensity with changing temperature and time. The release of doxorubicin from liposomes modified with poly(NIPAAm-co-AAm) copolymer was increased significantly, because poly(NIPAAm-co-AAm) could undergo the conformational transition in the narrow hyperthermia temperature region$(~40{\pm}2^{\circ}C)$. Moreover, we observed that doxorubicin released from liposomes within 5 minutes, and the size of modified liposomes was 120~170 nm. In this study, we have prepared temperature-sensitive liposomes which could be controlled by temperature. They can be applied in the field of a drug delivery system for tumor targeting by temperature control.
본 연구에서는 외부온열 온도$(~40^{\circ}C)$에서 항암약물(doxorubicin)이 방출되는 온도민감성 리포좀에 대하여 연구하였다. 온도민감성 리포좀은 외부온열온도에서 하한임계용액온도의 성질을 나타내는 N-isopropylacrylamide (NIP-AAm)와 Acrylamide(AAm)의 합성고분자에 의하여 변형되었다. 변형된 리포좀으로부터 약물(doxorubicin)의 방출은 온도와 시간의 변화에 따라서 형광강도를 측정하여 결정하였다. Poly(NIPAAm-co-AAm) copolymer에 의하여 변형된 리포좀으로부터 약물(doxorubicin)의 방출은 Poly(NIPAAm-co-AAm) copolymer가 온열온도 범위$(~40{\pm}2^{\circ}C)$에서 적절한 전이를 나타내기 때문에 증가하였다. 또한, 리포좀으로부터 약물의 방출은 5분 이내에 완료되었고, 변형된 리포좀의 크기는 120~170 nm 이었다. 본 연구에서는 온도에 의하여 제어 할 수 있는 온도민감성 리포좀을 제조하였다. 이것은 온도 제어에 따른 종양 표적화에 대한 약물전달시스템에서 활용 될 수 있을 것이다.