냉간금형용 합금강의 정밀입자가공에 의한 표면정밀도 향상

Improvement of Surface Morphology by Precision Particle Process for Cold Die Steel Alloy

Experimental study was conducted for lapping process after WEDMed specimen. In order to decide the lapping depth of the specimen, the number of the grain size was increased from 400, 600 to 800 to obtain the better surface. Observation of scanning electron microscope, hardness test, surface roughness test and energy dispersive spectrum(EDS) analysis were used for this experimental study. From the comparison and analyses of the results of between the wire-cut electrical discharge machining and the lapping, the following results were obtained. The surface roughness after lapping was found to be improved as increasing the number of lapping process like 1st, 2nd, 3rd lapping and the number of grain size such as 400, 600, 800. The surface hardness after increasing the lapping depth of the specimen was slowly increased. It was found that after 3rd lapping process the hardness was reached the hardness of original base material. It was found that the small amount of coating components within 3% was remained after the 1st lapping process, compared to that approximately 16% after WEDM process.