Optical and Long After-Glow Characteristics of $Eu^{2+}$, $Nd^{3+}$ doped $BaAl_{2}O_{4}$ Phosphorescent Crystals

($Eu^{2+}$, $Nd^{3+}$를 도핑시킨 $BaAl_{2}O_{4}$ 형광체의 광학 및 장잔광특성

  • Kim, Jeong-Hwan (Dept. of Industrial Chemical Engineering Chungbuk National University) ;
  • Kim, Byung-Gyu (Korea Institute of Geoscience and Mineral Resources) ;
  • Lee, Dong-Kyu (Dept. of Industrial Chemical Engineering Chungbuk National University)
  • Published : 2002.09.30

Abstract

In recent days, the study of a new phosphorescent phosphor has been performed in order to overcome the defect of sulfide phosphor and increase the brightness and long after-glow characteristic of phosphorescent phosphor. Particularly, sulfide phosphor usually used is so chemically unstable that the study of oxide phosphors are processing. $Eu^{2+}$, $Nd^{3+}$ doped Ba-Al-O phosphors sintered at $600{\sim}1500^{\circ}C$ for 2hours had the PL emission spectrum and after-glow over $1200^{\circ}C$. In this system, as the mole concentration of alumina increases, emission bands of phosphors moved from 500nm to 380nm. The optimum concentration of flux was 5wt% and after-glow characteristics of phosphors were found at the host material molar ratio ($BaCO_{3}:Al_{2}O_{3}$), 1:1 and 1:3.

Keywords

References

  1. T. Matsuzawa, Y. Aoki, N. Takeuchi, and Y. Muravama. J. Electronchem. Soc., 143, 2670 (1996) https://doi.org/10.1149/1.1837067
  2. II. YamaiTioto and T. Matsuzawa., J. Luminescence, 72-74, 287 (1997) https://doi.org/10.1016/S0022-2313(97)00012-4
  3. T. KatSLimata, T. Nabae, K. Sasajima, and T. Matszawa., J. Crystal Growth, 183, 361 (1998) https://doi.org/10.1016/S0022-0248(97)00308-4
  4. R. SaKai, T. Katsumata, S. Komuro. and T. Morikawa. J. Luminescence, 85, 149 (1999) https://doi.org/10.1016/S0022-2313(99)00061-7
  5. Bvoung-Byu Kim, Yeon-Tae Yu, Gi-Seong Eom, and Yong-Ki Lee, .J. Kor. Asso. Crystal Growth. 9, 315 (1999)
  6. T. Matsuzawa, K . Sasann-ia, T. Nabae S. Komuro, and T. Morikawa, J. Am. Ceram -Soc., 13, 413 (1999)
  7. Y. Lin, Z. Zhang, F. Zhang. Z. Tang, and Q. Chen, Material Chem. Physics, 65, 103 (2000) https://doi.org/10.1016/S0254-0584(00)00222-4
  8. H. Matsui, C. N, Xu, T. Watanabe, M. Akiyama, and X. G. Zheng, J. Electronchem. Soc., 147, 4692 (2000) https://doi.org/10.1149/1.1394125