Abstract
The pretreatment of tungsten added $BaTiO_x$ ceramics was performed to improve the recovery of Ba, Ti and W. $BaTiO_x$ ceramics were digested with HF : HCl ( 1 : 2 ) mixture in an acid digestion bomb at $220^{\circ}C$ for 3 hrs. The concentration of Ba, Ti and W were determined by ICP-AES. Recoveries of Ba, Ti and W were 99.6%, 99.8% and 99.2%, respectively. And their C.V. values were 1.02%, 0.73% and 1.79%. Using this method, the analytical results of Ba, Ti and W for a real sample were obainted to be 25.9% (w/w), 38.8% (w/w) and 3.31% (w/w), respectively.
텅스텐이 첨가된 $BaTiO_x$계 세라믹재료 중 Ba, Ti 및 W의 회수율을 증가시키기 위하여 가압 산 분해법을 이용하여 전처리하였다. $BaTiO_x$계 세라믹재료 시료를 가압 산 부내장치 내에서 HF : HCI ( 1 : 2 ) 혼합산을 가하여 $220^{\circ}C$에서 3시간동안 분해시킨 후 ICP-AES를 이용하여 Ba, Ti 및 W을 정량하였다. 그 결과 Ba는 99.6% Ti는 99.8% W는 99.2%의 회수율과 Ba는 1.02% Ti는 0.73% W는 1.79%의 C.V.값을 각각 얻었다. 이 전처리 방법을 실제시료에 적용하여 25.9% Ba38.8% Ti과 3.31% W 함량을 각각 구할수 있었다.