This paper presents experimental results for early-age properties of concrete such as the setting time and strength, evaluated via the ultrasonic pulse velocity (UPV). Developing and using an automatically-recording monitoring system, the UPV's of mortar and concrete with various water to binder ratios (W/B) were measured during the first 24 hours. In addition, probe penetration and compression tests were conducted to measure the setting time and compressive strength, respectively. It was observed that the UPV's of mortar with high W/B remained constant during the first 6.5 hours and then abruptly began to increase at constant rates. On the other hand, the UPV of mortar with low W/B increased relatively slowly and gradually due to the setting retardation caused by the use of high range water reducing agent (HRWR). It was found that setting of concrete occurs when the UPV reaches a certain value. Moreover, it was concluded that the estimation formulas should incorporate the effects of W/B to more accurately estimate the early-age strength of concrete from the UPV.
본 연구에서는 모르타르와 콘크리트의 초음파 속도를 자동적으로 측정할 수 있는 모니터링 시스템을 이용하여 물-결합재 비(W/B) 가 $0.27{\sim}0.50$인 모르타르와 콘크리트의 초음파 속도를 배합 직후부터 24시간까지 측정하였다. 또한, 용결 시간과 압축강도를 측정하기 위해 관입 저항 시험과 압축강도 시험을 각각 수행하였다. 실험결과로부터, 보통강도 콘크리트 배합의 초음파 속도는 배합 후 수 시간 동안에는 일정하다가 이후부터 갑자기 증가하는 경향을 보인 반면에, 고강도 콘크리트 배합에서는 고성능 감수제의 사용에 따른 응결 지연으로 초음파 속도가 서서히 증가하는 경향을 보였다. 그리고, 콘크리트의 응결은 초음파 속도가 소정의 속도에 도달했을 때 발생하는 것으로 나타냈다. 또한, 초음파 속도로부터 재령 3일 이하의 초기 강도 추정식에 W/B의 영향을 고려하면 보다 정확한 예측이 가능하리라 판단된다.