Fracture Strength of Porcelain Fused to Gold Crown & Gold Electroformed Crown

전기도금도재관과 금속도재관의 파절강도

The purpose of this study was to evaluate the fracture strength of porcelain fused to gold crown and gold electroformed crown according to incisal and incisal under 3mm. In this study, 28 gold electroformed crown and 28 porcelain fused to gold crown were fabricated. Fracture strength testing was carried out using an Instron 8871(Instron Corporation, U.S.A) at a cross head speed of 5mm/min. All of the measurements were statistically analyzed by Independent t-testing, and k-s testing. Statistical significance was set in advance at the probability level of less than 0.05. All measurements were analized with Windows $SPSS^{(R)}$ Version 10.0 software for the personal computer. The results of this study were as follows; 1. Comparison by location (1) A compared fracture strength of incisal and incisal under 3 mm, there was statistical significant difference between gold electro -formed crown and porcelain fused to gold crown (p<0.05). 2. Comparison by loading (1) When compared fracture strength of incisal, there was no significant difference between gold electroformed crown ($619.90{\pm}53.54N$)and porcelain fused to gold crown($674.68{\pm}87.42N$). (2) When compared fracture strength of incisal under 3 mm, there was significant difference between gold electroformed crown($688.29{\pm}14.88N$) and porcelain fused to gold crown($1931.81{\pm}29.64N$) (p<0.05). 3. Mode of fracture When compared of fracture mode, gold electroformed crown showed mode of fracture and fracture line reaching coping region and porcelain fused to gold crown showed only in porcelain region.