Conceptual Design of the Three Unit Fixed Partial Denture with Glass Fiber Reinforced Hybrid Composites

Glass fiber 강화 복합레진을 사용한 3본 고정성 국소의치의 개념 설계 연구

The results of the present feasibility study are summarized as follows, 1. The three unit bridge of knitted material and UD fibre reinforcement has both the rigidity and the strength against a vertical occlusal load of 75N. 2. Stress concentration at the junctional area between the bridge and the abutments, i.e. between the pontic and the knitted caps was observed. In the case of the bridge with reinforcement straps, it was partly shown that the concentration problem could be improved by simply increasing the fillet size at the area. Further refining in the surface of the junctional area will be needed to ensure a further improvement in the stress distribution. This will require some trade off in the level of the stress and the available space. A parametric study will help to decide the appropriate size of the fillet. 3. Design refinement is a must to improve the stress distribution and realize the most favourable shape in terms of fabrication. The current straight bar with a constant cross section area can be redesigned to a tapered shape. The curve from the dental arch should also be placed on the pontic design. In accordance with design refinement, the resistance of the bridge frame to other load cases should be evaluated. 4. Although not included in the present feasibility study, it is estimated that bridges of the anterior teeth can be made strong enough with the knitted material without further reinforcement using unidirectional materials. In this regard, a feasibility study on design concepts and stress analysis for 3, 4, 5 unit bridge is suggested. 5. Two types of bridge were analysed in terms of fatigue. The safe life design concept, i.e. fatigue design concept, looks reasonable for the bridge where if cracks should form and propagate there is virtually nothing a dentist to do. The bridge must be designed so that no crack will be initiated during the life span. In the case of crowns, however, if constructed with composite resin with knitted materials, it might be possible to repair them, which in general is impossible for crowns of PFM or of metal. Therefore for composite resin crowns, a damage tolerance design concept can be applied and reasonably higher operational stresses can be allowed. In this case, of course, a periodic inspection program should be established in parallel. 6. Parts of future works in terms of structural viewpoint which need to be addressed are summarized as the following: 1) To develop processing technology to accommodate design concepts; 2) More realistic modelling of the bridge and analysis-geometry and loading condition. Thickness variation in the knitted material, taper in the pontic, design for anterior tooth bridge, the effect of combined loads, etc, will need to be included; 3) To develop appropriate design concepts and design goals for the fibre composite FPD aiming at taking the best advantage of knitted materials, including the damage tolerance design concept; 4) To develop testing method and perform test such as static ultimate load test, fatigue test, repair test, etc, as necessary.

본 연구에서는 knitted glass fabric 강화 레진에 대한 치과보철소재로서의 적용가능성을 평가하기 위한 목적으로, 가장 높은 수준의 교합하중이 작용하게 되는 구치부 3본 고정성국소의치에 이 재료를 사용하는 경우에 대해 해석을 수행하였다. 우선 구치부3본 고정성국소의치에 대해 knitted glass fabric 강화 레진을 적용한 두 가지 설계 개념을 상정하였고, 각 설계형상에 대한 유한요소해석을 하였다. 강도 평가를 위해서75N의 생리적인 반복 수직 교합 하중 조건을 부여, 보철물에 유도되는 국소응력을 피로강도측면에서 고찰하였다. 각각의 설계에는 knitted glass fabric을 모재로 하고 보강재로 unidirectional 형의 glass 복합재가 사용되었다. 본 연구에서 개념설계 된 두 가지의 3본 고정성국소의치는 수직 교합 하중 75N 에 대해 충분한 강성과 강도를 가진 것으로 분석되었다. 가공치와 knitted caps사이의 연결 부위에서 국소적인 응력 집중이 관찰되었으나 그 크기는 재료의 피로강도 범위 이내였으며 국소적인 설계변경을 통하여 응력분포를 더욱 개선할 수 있을 것으로 추정하였다. 본 연구를 통해 knitted glass fabric 은 새로운 치과 보철 소재로서의 그 가능성이 기대된다.