Abstract
High fluidity concrete needs high dosage of superplasticizer to acquire sufficient fluidity and high contents of fine powder and viscosity agents to prevent segregation. But it requires high manufacturing cost and has difficult in quality control. Therefore, in this paper, determination of optimal mixture proportion of segregation type superplasticizer for high fluidity concrete and manufacturing high fluidity concrete by applying developed segregation reducing type superplasticizer are discussed using flowing concrete method. According to test results, as dosage of superplasticizer increases, it shows that fluidity and bleeding increase, while air contents and ratio of segregation resistance decrease. It also shows that adding viscosity agent into it reduce bleeding and improve segregation resistance. Dosage of AE agent into it containing viscosity agent recovers loss of air contents during flowing procedure. Combination of proper contents of superplasticizer, viscosity agent and AE agent make possible to develope segregation reducing type superplasticizer Compressive strength of high fluidity concrete applying flowing method with it is higher than that of base concrete. No differences of compressive strength between compacting methods are found.
고유동 콘크리트를 제조할 경우는 유동성 향상을 위한 다량의 고성능 감수제와 재료분리를 방지하기 위한 다량의 분체 혹은 증점제로 말미암아 제조비용이 고가이고, 또한 품질관리에도 많은 어려움이 있다. 그러므로, 본 연구에서는 유동성 및 재료분리 저항성이 우수한 고유동 콘크리트를 경제적으로 제조하기 위하여 분리저감형 유동화제의 최적배합비를 결정한 다음, 유동화 공법으로 접근하는 것을 검토하였다. 실험결과로 유동화제 첨가량이 증가할수록 유동성 및 블리딩량은 증가하였고, 공기량 및 재료분리저항성은 저하하는 것으로 나타났다. 따라서, 여기에 증점제를 첨가함에 따라 양호한 유동성에서 블리딩량이 저하하였고, 재료분리저항성도 증대되었는데, 마지막으로 AE제량 증가에 따라 저하된 공기량이 회복되므로써 양질의 분리저감형 유동화제로 최적배합비를 결정할 수 있었다. 경화 콘크리트 특성으로 유동화 공법으로 제조된 고유동 콘크리트의 압축강도는 베이스 콘크리트보다 증가하는 것으로 나타났고, 무다짐 공시체의 압축강도는 표준다짐 공시체의 압축강도와 유사한 것으로 나타나 다짐 방법간의 차이는 없는 것으로 나타났다.