Abstract
The piezoelectric thin film sensor has good characteristics to observe the impact responses of composite structures. The capabilities for monitoring impact behavior of Gr/Ep laminates subjected to damage-induced impact using the PVDF(polyvinylidene fluoride) film sensor were examined. For a series of low-velocity impact tests from low energy to damage-induced energy, simulated sensor signals were compared with measured signals and the PVDF film sensor. Local impact damages(matrix cracking and delamination) were found at three impact tests, but the measured signals agreed well with the simulated sensor signals based on the linear relationship between the impact forces and the PVDF film sensor signals. And the inverse technique was applied to reconstruct the impact forces using the PVDF film sensor signals. Most of reconstructed impact forces had good agreement with the measured forces. The comparison results showed that the local damage due. to low-velocity impact didn't disturb the global impact responses of composite laminates and the reconstruction of impact forces from PVDF sensor signals wasn't affected by the local damage.
압전필름센서는 복합재 구조물의 저속충격응답을 관측하기에 우수한 특성을 지니고 있다. 본 연구에서는 Gr/Ep 복합재 적층판이 손상이 발생할 수 있을 정도의 충격에너지를 받았을 때 압전필름센서 신호를 이용하여 충격거동을 모니터링할 수 있는 가능성에 대하여 고찰하였다. 손상이 발생하지 않는 저에너지 충격조건부터 국부적인 손상을 유발할 수 있는 충격조건까지 압전필름센서가 부착된 Gr/Ep 복합재 적층판에 대하여 16가지의 저속충격시험을 수행하였다. 세 가지 조거의 충격시험에서 기지균열 및 층간분리 등의 국부적인 손상이 발생하였으나, 충격력과, 변위, 변형률, 압전센서 신호와의 관계를 이용한 선형해석 모델을 사용하여 충격하중에 의한 복합재 적층판의 응답을 예측하는 정방향 문제와 압전센서 신호로부터 충격력을 복원하는 역방향 문제에서 시험과 해석 결과는 비교적 잘 일치하는 경향을 보였다. 복원된 충격력으로부터 국부적인 손상이 발생할 정도의 충격까지는 압전필름센서 신호를 이용하여 충격력을 정확히 복원할 수 있음을 확인하였다.