마이크로 솔더 범프의 전단강도와 시효 특성

Aging Characteristic of Shear Strength in Micro Solder Bump

  • 발행 : 2002.10.01

초록

Flip-chip interconnection that uses solder bump is an essential technology to improve the performance of microelectronics which require higher working speed, higher density, and smaller size. In this paper, the shear strength of Cr/Cr-Cu/Cu UBM structure of the high-melting solder b01p and that of low-melting solder bump after aging is evaluated. Observe intermetallic compound and bump joint condition at the interface between solder and UBM by SEM and TEM. And analyze the shear load concentrated to bump applying finite element analysis. As a result of experiment, the maximum shear strength of Sn-97wt%Pb which was treated 900 hrs aging has been decreased as 25% and Sn-37wt%Pb sample has been decreased as 20%. By the aging process, the growth of $Cu_6Sn_5$ and $Cu_3Sn$ is ascertained. And the tendency of crack path movement that is interior of a solder to intermetallic compound interface is found.

키워드

참고문헌

  1. International Technology Readmap for Semiconductor(1999 edition)
  2. Proceeding of Surface Mount International Confefence Enhancement of Underfill Encapsulants for Flip-Chip Technology M.B. Vincent;C.P. Wong
  3. Journal of Electronic Materials v.28 no.9 The Effects of Underfill on the Reliability of Flip Chip Solder Joints Peng Su;Sven Rzepka https://doi.org/10.1007/s11664-999-0178-8
  4. IEEE Transactions on Components Package and Manufacturing Technology-Part B v.20 no.2 Aging Studies of Cu-Sn Intermetallic Compounds in Annealed Surface Mount Solder Joints AlexC, K.So https://doi.org/10.1109/96.575568
  5. The Effect of Stud Structure and Eutectic Solder Electroplating on Intermetallic Growth and Reliability of Flip-Chip Solder Bump Guowei Xiao;Philip Chah
  6. Acta Metall. K.N. Tu
  7. IMAPS v.9 no.1 Aging Characteristic of Intermetallic Compounds and Bonding Strength of Flip-Chip Solder Bump Kyung Seob Kim;Eui Goo Chang;Yong Bin Sun
  8. J. Kor. Inst. Met. & Mater. v.37 no.11 Interfacial Reaction of Sn-3.5wt%Ag Solder Alloy with a Variance of Ni layer Thickness Won Kyoung Choi;Hyuck Mo Lee