Study of Order-Disorder Phase Transition of $(Fe_{0.61}Ni_{0.39})_3V$V Alloy by Neutron Diffraction Method

중성자회절법을 이용한 $(Fe_{0.61}Ni_{0.39})_3V$ 합금의 규칙- 불규칙 상전이 연구

  • 이정수 (한국원자력연구소 하나로이용기술개발팀) ;
  • 이창희 (한국원자력연구소 하나로이용기술개발팀)
  • Published : 2002.03.01

Abstract

The order-disorder phase transition of (Fe/sub 0.61/Ni/sub 0.39/)₃V alloy that is annealed at various temperatures and time conditions was sty(lied with the examination of long-range order parameter(S) by using neutron diffraction method. As a result, the structure of the sample annealed at 680℃ for 94 h was not changed; that is, it existed iii perfect disordered state and showed face-centered cubic structure. Otherwise, samples which were annealed at temperature below 640℃ showed the value of long-range order parameter with 0 < S < 1 and phase transition into simple cubic structure partly. It was found that the annealed sample at 465℃ for 144 h is the most approximated to the thermal equilibrium state from the S-T/T/sub c/ related equation of Cowley.

중성자회절법을 이용하여 여러 다른 조건으로 열처리한 (Fe/sub 0.61/Ni/sub 0.39/)₃V 합금 분말시료의 장거리 규칙도를 측정하여 규칙-불규칙 상전이의 정도를 조사하였다. 조사 결과 680℃-94 h 열처리 시료는 완전 불규칙 상태로 상전이가 발생하지 않았으며 면심입방구조를 보였다. T < 640℃의 조건에서 열처리한 시료들은 모두 장거리 규칙도 0 < S < 1으로 면심입방구조의 일부가 단순입방구조로 상전이 함을 보여주었다. 또한 Cowley의 S-T/T/sub c/ 관계식으로부터 465℃-144 h 으로 열처리한 시료가 열평형상태에 가장 근접하였음을 확인하였다

Keywords

References

  1. Liu, C. T., Int. Metals Rev., 29(3), 168, (1984)
  2. Bacon, G. E., Neutron Diffraction, Clarendon, Oxford (1975)
  3. Bragg, W. L. and Williams, E. J., Proc. Roy. Soc., A145, 699 (1934)
  4. Batterman, B. W., J. Appl. Phys., 38, 556 (1957)
  5. Goman'kov, V. I., Puzei, I. M. and Loshmanov, A. A., Soc. Phys. Cryst., 10, 338 (1965)
  6. Cowley, J. M., Phys. Rev., 77(5), 669 (1950)