Abstract
In this work, the effect of fusible interlining on the appearance related properties and mechanical characteristics of Lyocell fabric after fusing was investigated. Two different types(20's and 10's) of Lyocell face fabric with six different interlining(by thickness and structure) for earth Lyocell fabric were examined. In order to establish the optimum fusing condition for the different face fabric and interlining, peel strength of each fused fabric was measured, which was dependent on the fusing temperature, pressure, and time. The characteristics related appearance and mechanical characteristics of each fused fabric were determined. The results are as follows: The peel strength was excellent, when the fabric was fused with the force of 3kgf/$textrm{cm}^2$ at $120^{\circ}C$ for 15seconds. Flex stiffness, G, 2HG, 2HG5(shear), B, 2HB(bending) of 100% Lyocell fabric 10's were higher than those of 100% Lyocell 20's. Flex stiffness, crease recovery, G, 2HG, B, 2HB of thicker woven interlining were higher than those of thinner woven interlining. Crease recovery of twill interlining were higher than those of plain interlining. In case of shear and bending properties, however, plain interlining was higher than twill interlining. Flex stiffness, crease recovery, G, 2HG, 2HG5, B, 2HB of nonwoven interlining were higher than those of woven interlining. In case of drapability, however, woven interlining was higher than nonwoven interlining.