Stacking Sequence Effects on Indentation Damage Behaviors of Fiber Metal Laminate

섬유의 적층 각도에 따른 섬유 금속 적층판의 압입 손상 거동

  • 한경섭 (포항공과대학교 기계공학과) ;
  • 남현욱 (포항공과대학교 기계공학과 박사 후 연구원) ;
  • 정성욱 (포항공과대학교 기계공학과)
  • Published : 2002.05.01
Download PDF
⟨ Previous Next ⟩

Abstract

In this research, the effects of fiber stacking sequence on damage behaviors of FML(Fiber Metal Laminates) subject to indentation loading. SOP (Singly Oriented Ply) FML and angle ply FML were fabricated to study fiber orientation effects and angle ply effects. FML were fabricated by using 1050 aluminum laminate and carbon/epoxy prepreg. To increase adhesive bonding strength, Al laminate was etched using FPL methods. The static indentation test were conducted by using UTM under the 2side clamped conditions. During the tests, load and displacement curve and crack initiation and propagation behaviors were investigated. As fiber orientation angle increases, the crack initiation load of SOP FML increases because the stiffness induced by fiber orientation is increased. The penetration load of SOP FML is influenced by the deformation tendency and boundary conditions. However, the macro-crack of angle ply FML was initiated by fiber breakage of lower ply because angle plies in Angle ply FML prevents the crack growth and consolidation. The Angle ply FML has a critical cross-angle which prevent crack growth and consolidation. Damage behavior of Angle ply FML is changed around the critical cross-angle.

Keywords

References

  1. Asundi, A. and Choi, Alta Y.N., 1997 'Fiber Metal Laminates:An Advanced Material for Future Aircraft,' J. of Mat. Processing Tech., Vol. 63, pp. 384-394 https://doi.org/10.1016/S0924-0136(96)02652-0
  2. 이제헌, 김영환, 2000, 'Al 7075/CFRP 적층 복합재료 제조를 위한 전처리 조건과 경화방법 연구,' 한국복합재료학회지 제 13 권 제 4 호, pp. 42-53
  3. 남현욱, 변현중, 정성욱, 한경섭, 2001, '집중하중을 받은 일방향 보강 섬유 금속 적층판의 손상 개시 모델링' 한국복합재료학회지 제 14 권 제 3 호, pp. 42-50
  4. Chen, J.L. and Sun, C.T., 1989, 'Modeling of Orthotropic Elastic-Plastic Properties of ARALL Laminate,' Composites Sci. & Tech., Vol. 36, pp. 321-337 https://doi.org/10.1016/0266-3538(89)90045-6
  5. Kawai, M. et al., 1998, 'Inelastic Behavior and Strength of Fiber-Metal Hybrid Composite: GLARE,' Int. J. Mech. Sci, Vol. 40, Nos. 2-3, pp. 183-198 https://doi.org/10.1016/S0020-7403(97)00048-9
  6. Hong, S. and Liu, D., 1989, 'On the Relationship Between Impact Energy and Delamination Area,' Exp. Mech., pp. 115-120 https://doi.org/10.1007/BF02321362
  7. Collombet, F. et al., 1998, 'Damage Criteria for the Study of Impacted Composite Laminates,' Composites Sci. and Tech., Vol. 58, pp. 679-686 https://doi.org/10.1016/S0266-3538(97)00145-0
  8. de Freitas, M. and Reis, L., 1998, 'Failure Mechanisms on Composite Specimens Subjected to Compression after Impact,' Comp. Struct., Vol.42, pp. 365-373 https://doi.org/10.1016/S0263-8223(98)00081-6
  9. Strait, L., Karasek, M., Amateau, M., 1992 'Effects of Stacking Sequence on the Impact Resistance of Carbon Fiber Reinforced Thermo-Plastic Toughened Epoxy Laminates,' J.of Comp. Mat., Vol. 26, pp. 725-740 https://doi.org/10.1177/002199839202601202
  10. Willis, J. R., 1966, 'Hertzian Contact of Anisotropic Bodies,' J. of Mech. and Physics of Solids, Vol. 14, pp. 163-176 https://doi.org/10.1016/0022-5096(66)90036-6
  11. Vlot, A., 1996, 'Impact Loading on Fiber Metal Laminates,' Int. J. Impact Engng, Vol. 18, No. 3, pp. 291-307 https://doi.org/10.1016/0734-743X(96)89050-6
  12. Lawcock, G.D. et al., 1997, 'Effects of Fiber/Matrix Adhesion on Carbon Fiber Reinforced Metal Laminates-II. Impact Behavior,' Compo. Sci. & Tech., Vol. 57, pp. 1621-1628 https://doi.org/10.1016/S0266-3538(97)00094-8
  13. Wegman, Raymond F., 1989, Surface Preparation Techniques for Adhesive Bonding, Noyes Publications